zirconium ceramic beads was made by zirconium silicate powder through a unique formula, special production process and pretreatment, then it is made by more than 2000°C high temperature phase method. Especially it suitable for the shot blasting during the process of metal parts production and maintenance and peen forming of light alloy components.
Quality Grade |
Chemical component |
Specific density |
Bulk density |
|
Export |
ZrO2:60~65% |
3.85g/cm3 |
2.3g/cm3 |
|
SiO2:30~35% |
||||
Hardness |
HV |
Mohs |
HRC |
|
700HV |
7.0 |
60HRC |
||
Manufacturing technique |
Fusion method |
|||
Size range(mm) |
B20 0.600~0.850mm |
B80 0.180~0.250mm |
B170 0.045~0.090mm |
|
B30 0.425~0.600mm |
B100 0.125~0.180mm |
B205 0.000~0.063mm |
||
B40 0.250~0.425mm |
B120 0.063~0.125mm |
B400 0.030~0.063mm |
||
B60 0.125~0.250mm |
B125 0.000~0.125mm |
B505 0.010~0.030mm |
zirconium ceramic beads Features:
Reduced beads consumption (10-20times).
-Lower metal surface roughness-zirconium silicate ceramic beads.
-Less operating pressure and reduced abrasive velocity needed. Thus have far less abrasive breakdown and dust generation, results in cleaner working environment and better operator visibility.
-White color, high sphericity and smooth surface beads-zirconium ceramic beads.
-Strong mechanical resistance and high toughness, but gentle with equipment and tools preserving work parts.
-Chemically inert, no metallic contamination for treated parts.
zirconium ceramic beads Application:
zirconium ceramic beads can be used in these applications (just name a few):
- Cleaning and surface preparation (deburring, etching, paint removal and cosmetic finishing …)Of moulds, castings and delicate items.
-Effectively used in air or wet pressure blasting process and in wheel turbine machines.
Supply Ability:100Ton per Month or according to customers requirment