platinized and mmo mixed metal oxide ruthenium iridium titanium electrode plate titanium anode for alkaline water electro
About Titanium Anode
Titanium Substrate | Grade | N | C | H | Fe | O | Ti |
1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | bal | |
2 | 0.03 | 0.05 | 0.015 | 0.3 | 0.25 | bal | |
Regular Coating | Platinum:0.5um/1um; Mixed Iridium and Platinum:0.5um/1um; Mixed Ruthenium and Iridium:6-8um; Mixed Iridium and Tantalum:6-8um. | ||||||
Characteristics | Coating: Mixed Ruthenium and Iridium; Chlorine evolution potential: <1.13V; Polarizability: ≤40mv; Accelerated life: ≥3000min under current density 1000A/m2; Anode strengthening weightlessness: ≤10mg; Suitable working environment: Solution contains Cl-, PH<=7 | ||||||
Coating contents & life span | 8 grams/m2: >6,000 hours; 10 grams/m2: > 8,000 hours; 12 grams/m2: >10,000 hours; 15 grams/m2: >12,000 hours; 20 grams/m2: >15,000 hours | ||||||
Working parameters | Current density: <600A/m2; Temperature: 40-60°C; Chlorine concentration: About 30~50grams/liter; Polarity reversal: suitable; Reversal frequency: 2-4 hours | ||||||
Regular sizes | 63.5*150mm, 13pcs/set; 64*110mm, 7pcs/set; 80*120mm, 1pcs/set; 30*183mm, 7pcs/set; 80*185mm, 7pcs/set | ||||||
Applications |
1.Water ionizer or water electrolysis a. Making alkaline and acidic water
2.Waste water treatment a.Organic sewage treatment, b. Chemical sewage treatment, c. Pesticide sewage treatment, d. Drinking water disinfection, e. Bleaching & dyeing, f. Swimming pool g. Hospital sewage treatment, h. Food industry disinfection etc.
3.Sodium Hypochlorite Generator & Chlorinator a. Swimming pool water treatment b. Water sterilization & water purification,
4.Sea water electrolysis or Electrodialysis a. Desalination, b. Material recycling in the waste water, c. Paper making, *Chemical, medical industry, d. Light industry, *Metallurgy, e. Making fresh water, etc.
5.Chlor-Alkali Industry
6.Electroplating a. Electrolating Au,Cr,Zn,Cu.etc
7.MMO Cathodic Protection |
Quality Contro
Product coating show
Titanium anode is a kind of electro-catalysis electrode in electro-chemistry, which is composed by substrate that is pure titanium and coated that is precious metal oxide.
1. Substrate treatment: it needs to be treated by roughing, cleaning and removing oil, which can increase the compactness of catalytic.
2. Brushing & Drying:After substrate treatment, it will be proceeded brush coated. The main coated content is platinum group metal, which is a kind of mixed solution.
3. Heat Treatment:Heat treatment will be proceed after drying.
The whole procedure need to be repeated many times. This method is better to form thin oxide catalytic that is lamellar adhere to substrate surface.