Densityρ: | 2.23± 0.02g/cm3 |
Hardness: | >7 |
Tensile strength: | 4.8×107Pa(N/M2) |
Bulk modulus: | 93×103 M pa |
Modulus of rigidity: | 3.1×1010Pa |
Young's modulus: | 63KN/mm3 |
Compressive strength: | 1200kg/ cm2 |
Poisson's ratio: | 0.18 |
Thermal expansion coefficient: | (0-300℃) (3.3±0.1)x10-6K-1 |
Coefficient of thermal conductivity: | 1.2W×(m×k) -1 |
Specific heat capacity: | (20-100℃) 00.82kJx(kgxk) |
Light transmittance: | 92% |
The refractive index: | Nd: 1.47384 |
The wavelength: | 435.8nm=1.481, 79.9nm=1.4772, 546.1nm=1.4732 |
Softening point: | 810±10 ℃ |
The resistivity1gρ | 250℃ 8.0Ω×cm |
Dielectric coefficientε | 4.7 |
Dielectric strength | 5 ×107V/M |
Dielectric loss factor | tanσ(MC20℃)≤38 ×10-4 |
Resistance to cold and hot shock | 280℃ |
Continuous working temperature | ≤550℃ |