Feature | High hardness with a soft core giving resistance to shock load & excellent resistance to surface wear | ||||||||
Hardness | Hardness is HRC 60min.Reference the accompanying chart for minimum case depth | ||||||||
Size Available | 1mm-50.8mm | ||||||||
Grade Available | G100;G200;G500;G1000 | ||||||||
Application | automotive applications,semiprecision bearings, and commercial applications such as castors,locks,drawer slides, bicycles,and conveyors | ||||||||
Material Conversion | ASTM/AISI | DIN | W-Nr | NF | JIS | ||||
1010/1015 | CK10/CK15 | 1.1121/1.2241 | XC10/XC15 | S10C/S15C |
Shot Name | In | mm | Shot Name | In | mm |
9 | 0.08 | -2.03 | 3 | 0.14" | -3.56 |
8½ | 0.085 | -2.16 | 2 | 0.15" | -3.81 |
8 | 0.09 | -2.29 | 1 | 0.16" | -4.06 |
7½ | 0.095 | -2.41 | B | 0.17" | -4.31 |
7 | 0.1 | -2.54 | BB | 0.18" | -4.57 |
6 | 0.11 | -2.79 | TT | 0.21" | -5.33 |
5 | 0.12 | -3.05 | TTT | 0.22" | -5.588 |
4 | 0.13 | -3.3 |
Feaure | Universal material for ball and roller bearing industry.Chrome steel balls contain chromium and to through hardening has an excellent surface quality and load bearing | ||||||||
Hardness | Excellent hardness control with a through hardness of HRC 60 to 67 | ||||||||
Size Avaliable | chrome steel ball 1mm-100mm | ||||||||
Grade | G10 G20 G40 G60 G100 G200 G500 G1000 | ||||||||
Application | Universal for many applications. For example: balls & roller bearings.Linear monition, Balls lead screws, grinding media. | ||||||||
Material Conversion | ASTM/AISI | DIN | W-Nr | NF | JIS | ||||
52100 | 100Cr6 | 1.3505 | 100C6 | SUJ2 | |||||
Carbon | Chromium | Manganese | Silicon | Sulfur | Phosphorous | ||||
0.98% to 1.10% | 1.30% to 1.60% | 0.25% to 0.45% | 0.15% to 0.35% | 0.025% maximum | 0.025% maximum |
Material | Feature | General Applications |
AISI420 | Magnetic, Harden-able, fair corrosion resistance | used for special bearings and valves where Balls requiring a combine action of hardness and corrosion resistance |
AISI440C | Magnetic, highest hardness, good corrosion resistance | used in bearing nozzles and valves where lubrication is poor or absent |
AISI304 | austentitic, corrosion resistance, slightly magnetic, however annealing can makes it non - magnetic | Used in valves and relevant application,food products, aerosols, home sprays,perfumes and medical equipment. |
AISI316 | non - magnetic, good corrosion resistance even when exposed to marine atmosphere and sulfuric acid | used in presence of sulphuric, phosphoric and acetic acids.Mainly used in chemical,paper and textile industries |
AISI316L | Characteristics same as 316 but with excellent corrosion resistance, Lower carbon content than regular 316. | expecially used in Jewelry, and Human Implant Applications |
Name | Ceramic Balls | Size | 0.8mm-150mm | ||
Materials | ZrO2, Si3N4, Al2O3 etc.. | Color | White, Grey, Black, Yellow | ||
Grade | G5 G10 | Standard | ANSI, DIN, ISO, JIS | ||
Advantage | High Temperature Resistance, High Corrosion Resistance, High Abrasion Resistance, Electrical Resistivity, and Self-Lubrication. | ||||
Useage | Chemical Industry, Metallurgy, Petroleum, Electronics Fields etc |