Dimensional accuracy | Up to 0.01mm | |
Smoothness | Highest possible mirror | |
Concentricity | Up to 0.01mm | |
Parallelism | Up to 0.01mm | |
The inner hole tolerance | The minimum 0.01mm | |
Straight flute | The narrowest 0.1x100mm | |
The thickness of the size | Minimum to 0.2mm | |
The screw thread | Minimum internal thread M2 | |
Cylindricity | Up to 0.01mm | |
The linear tolerance | Up to 0.01mm | |
The smallest aperture | The minimum 0.07mm | |
Precision process | CNC maching,grinding,lapping | |
Surface finish | Glazed,polishing or metallized | |
Visual quality: 1. No cracks, no dark dots, no contamination and sharp edges; 2. Evenly distributed glaze with very smooth surface | ||
Property | Units | |||||||
Al2O3 Content | % | 96 | 98 | 99.5 | 99.7 | |||
Density | g / cm3 | 3.70 | 3.80 | 3.90 | 3.92 | |||
Color | - | White | White | Ivory | Ivory | |||
Compressive Strength @ 25 C | Mpa | 2229 | 2091 | 2512 | 2350 | |||
Tensile Strength @ 25 C | MPa | 200 | 200 | 248 | 252 | |||
Flexural Strength @ 25 C | MPa | 331 | 276 | 324 | 320 | |||
Elastic Modulus @ 25 C | GPa | 290 | 331 | 366 | 380 | |||
Hardness : Knoop Rockwell | (Gpa) Kg/mm2 R45N | (11.7) 1196 79 | (12.5) 1276 77 | (14) 1428 85 | (15) 1510 90 | |||
Thermal Conductivity @ 25 C | W / m-Deg K | 20.8 | 28.1 | 30.7 | 31.6 | |||
Coefficient of Thermal Expansion @ 25-1000 C | 1 X 10-6 / Deg C | 7.9 | 8.5 | 8.1 | 8.0 | |||
Specific Heat @ 25 C | cal / g / Deg C | .184 | .184 | .182 | .180 | |||
Maximum Working Temp. | Deg C | 1650 | 1650 | 1700 | 1700 | |||
VolumeResitivity @25C @700 C | ohm-cm ohm-cm | 1 X 10-13 1 X 10-8 | 1X 10-13 2.2 X 10-9 | 1 X 10-13 6 x 10-7 | 1 X 10-13 6 x 10-7 | |||
Dielectric Strength (@Thickness) 100Mils | ac volts per mil | 350 | 340 | 335 | 330 | |||
Dielectric Constant 1Mhz @25C | e' / eo | 8.6 | 9.4 | 9.7 | 10.0 | |||
Dissipation Factor 1 Mhz @25C | Tan Delta | .0004 | .0003 | .0003 | .0002 |