Properties | TEST METHOD | UNIT ENGLISH METRIC | 20mil HD 0.5mm | 30mil HD 0.75mm | 40mil HD 1.0mm | 50mil HD 1.25mm | ||||||
Thickness | ASTM D 5199 | mil(mm) | 20(0.50) | 30(0.750) | 40(1.00) | 50(1.25) | ||||||
Density | ASTM D 1505 | g/cm3 | 0.940 | 0.940 | 0.940 | 0.940 | ||||||
Tensile Properties(Each Direction) | ASTM D 6693,Type IV | |||||||||||
Strength at break | Dumbell,2 ipm | lb/in-width(N/mm) | 96(17) | 114(20) | 152(27) | 188(33) | ||||||
Strength at yield | lb/in-width(N/mm) | 51(9) | 63(11) | 84(15) | 102(18) | |||||||
Elongation at Break | G.L.2.0in(50mm) | % | 700 | 700 | 700 | 700 | ||||||
Elongation at Yield | G.L.1.3in(33mm) | % | 12 | 12 | 12 | 12 | ||||||
Tear Resistance | ASTM D 1004 | lb(N) | 18(80) | 21(93) | 28(125) | 35(156) | ||||||
Puncture Resistance | ASTM D 4833 | lb(N) | 45(200) | 54(240) | 72(320) | 90(400) | ||||||
Carbon Black Content | ASTM D 1603*4218 | %(range) | 2.0-3.0 | 2.0-3.0 | 2.0-3.0 | 2.0-3.0 | ||||||
Carbon Black Dispersion | ASTM D 5596 | Note(1) | Note(1) | Note(1) | Note(1) | |||||||
Notched Constant Tensile Load | ASTM D 5397,Appendix | hr | 300 | 300 | 300 | 300 | ||||||
Oxidative Induction Time | ASTM D 3895,200℃;O2,1atm | mins | >100 | >100 | >100 | >100 | ||||||
TYPICAL ROLL DIMENSIONS | ||||||||||||
Roll Length | ft(m) | 1,120(341) | 1,120(341) | 870(265) | 720(219) | |||||||
Roll Width | ft(m) | 22.5(6.86) | 22.5(6.86) | 22.5(6.86) | 22.5(6.86) |
Properties | TEST METHOD | UNIT ENGLISH METRIC | 60mil HD 1.5mm | 80mil HD 2.0mm | 100mil HD 2.5mm | 120mil HD 3.0mm | ||||||
Thickness | ASTM D 5199 | mil(mm) | 60(1.50) | 80(2.00) | 100(2.50) | 120(3.00) | ||||||
Density | ASTM D 1505 | g/cm3 | 0.940 | 0.940 | 0.940 | 0.940 | ||||||
Tensile Properties(Each Direction) | ASTM D 6693,Type IV | |||||||||||
Strength at break | Dumbell,2 ipm | lb/in-width(N/mm) | 228(40) | 304(53) | 380(67) | 457(80) | ||||||
Strength at yield | lb/in-width(N/mm) | 126(22) | 168(29) | 210(37) | 251(44) | |||||||
Elongation at Break | G.L.2.0in(50mm) | % | 700 | 700 | 700 | 700 | ||||||
Elongation at Yield | G.L.1.3in(33mm) | % | 12 | 12 | 12 | 12 | ||||||
Tear Resistance | ASTM D 1004 | lb(N) | 42(187) | 56(249) | 70(311) | 84(374) | ||||||
Puncture Resistance | ASTM D 4833 | lb(N) | 108(480) | 144(640) | 180(800) | 215(960) | ||||||
Carbon Black Content | ASTM D 1603*4218 | %(range) | 2.0-3.0 | 2.0-3.0 | 2.0-3.0 | 2.0-3.0 | ||||||
Carbon Black Dispersion | ASTM D 5596 | Note(1) | Note(1) | Note(1) | Note(1) | |||||||
Notched Constant Tensile Load | ASTM D 5397,Appendix | hr | 300 | 300 | 300 | 300 | ||||||
Oxidative Induction Time | ASTM D 3895,200℃;O2,1atm | mins | >100 | >100 | >100 | >100 | ||||||
TYPICAL ROLL DIMENSIONS | ||||||||||||
Roll Length | ft(m) | 560(171) | 430(131) | 340(104) | 164(50) | |||||||
Roll Width | ft(m) | 22.5(6.86) | 22.5(6.86) | 22.5(6.86) | 22.5(6.86) |