ABS PA-757 | ||||||||
ABS PA -757 (Natural) | ||||||||
Features | Applications | |||||||
Non-halogen Flame Retardant Balance Performance | Home Appliances E & E | |||||||
Properties | Test Standart | Text Condition | Units | Typical Values | ||||
Physical Properties | ||||||||
Mass Density | D792 | 23°C | 1.05 | |||||
Melt Flow Rate | D1238 | g/10min | 1.6 | |||||
Hardness | D785 | 23°C | R Scale | 116 | ||||
Tensile Strength (Yield) | D638 | 6 mm/min | Kg/cm2/b/in | 470/6660 | ||||
Tensile Elongation | D638 | 6 mm/min | % | 25 | ||||
Flexural Strength | D790 | 2.8mm/min | Kg/cm2/lb/in2 | 790/11660 | ||||
Flexural Modulus | D790 | 2.8mm/min | 104 Kg/cm2/105 lb/in2 | 2.7/3.8 | ||||
IZOD Impact Notched | D256 (Notched) | 6.4 mm, 23℃ | Kg-cm/cm/ft-lb/in | 20/3.7 | ||||
3.2 mm, 23℃ | Kg-cm/cm/ft-lb/in | 21/3.9 | ||||||
Vicat Softening Temp. | D1525 | 1 Kg,50 ℃/hr | °C | 105 | ||||
H.D.T | D648 | 1.8 MPa Annealed/ 1.8MPa Unannealed | °C | 95/ 85 | ||||
UL Flammability | UL94 | 3.0mm/1.5mm | 1.5 mm HB |