Properties | Testing Method | Unit | 2015GF | 2030GF | 2033GF | 2001T | 2004T | 2020CF | 2030GFR |
GF15 | GF30 | GF33 | Low Impact | High Impact | CF20 | GF30 with FR | |||
Density | ISO 1183-1 | g/cm3 | 1.23 | 1.36 | 1.38 | 1.11 | 1.07 | 1.21 | 1.42 |
Tensile Strength | ISO 527 | MPa | 130 | 195 | 200 | 70 | 50 | 225 | 170 |
Elongation at Break | ISO 527 | % | 2.5 | 2.5 | 2 | 15 | >45 | 2.5 | 2.5 |
Tensile Modulus of Elasticity | ISO 527 | MPa | 6000 | 9500 | 10000 | 2800 | 2000 | 16000 | 10000 |
Flexural Strength | ISO 178 | MPa | 210 | 290 | 300 | 100 | 75 | 310 | 270 |
Flexural Modulus | ISO 178 | MPa | 5000 | 8600 | 9200 | 2500 | 1850 | 12000 | 9500 |
Charpy Notched Impact Strength | ISO 179 | kJ/m2 | 6 | 11 | 12 | 12 | 80 | 7 | 9 |
HDT 1.80MPa | ISO 75-2 | ℃ | 235 | 250 | 250 | 70 | 55 | 250 | 240 |
1.80MPa | |||||||||
Melting Point | ISO 11357 | ℃ | 255 | 255 | 255 | 255 | 255 | 255 | 255 |
Flammability | UL94 | - | HB | HB | HB | HB | HB | HB | 255 1.5mm |
1.5mm |