Physical properties of PA6 and PA66 | ||||||||||||||||||
project | unit | PA6 | PA66 | |||||||||||||||
Enhance the level | Enhance the level | Enhanced flame retardant grade | ||||||||||||||||
GF 15% | GF 30% | GF 50% | GF 15% | GF 30% | GF 15%FR | GF 30%FR | ||||||||||||
The proportion of | 1463 | g/m² | 1.25 | 1.37 | 1.52 | 1.31 | 1.37 | 1.34 | 1.5 | |||||||||
The tensile strength | 1040-92 | Mpa | 90 | 142 | 165 | 145 | 165 | 100 | 120 | |||||||||
Elongation at break | 1040-92 | % | 4 | 4 | 3 | 4 | 2 | 4 | 3 | |||||||||
The bending strength | 9341-2000 | Mpa | 160 | 238 | 275 | 240 | 265 | 182 | 205 | |||||||||
Bending modulus | 9341-2000 | Mpa | 5000 | 7000 | 10015 | 7500 | 7600 | 6500 | 7000 | |||||||||
LZOD notch impact strength | 1040-93 | Kj/m² | 10 | 22 | 23 | 13 | 18 | 10.6 | 14 | |||||||||
Melting point index | 3682-2000 | g/10min | / | / | / | / | / | / | / | |||||||||
Forming shrinkage rate | 15585-95 | % | 0.5-0.9 | 0.4-0.8 | 0.3-0.6 | 0.4-1.1 | 0.4-0.9 | 0.5-1.1 | 0.4-0.9 | |||||||||
Thermal deformation temperature HDT(1.82 MPa) | 1634-2004 | ℃ | 205 | 220 | 230 | 245 | 260 | 250 | 255 | |||||||||
Flame retardant grade | UL94 | - | HB | HB | HB | HB | HB | V-0 | V-0 | |||||||||
Note: This data is typical value, only for material selection reference. For specific use, please consult our material engineer. |