Top quality W-NI-Fe tungsten alloy bars tungsten rods from Chinese manufacture

Grade

AMS-T-21014

Class 1

Class 1

Class 2

Class 2

Composition

90W7Ni3Fe

91W6Ni3Fe

92W5Ni3Fe

93W4Ni3Fe

Density (g/cm3)

17.1±0.15

17.25±0.15

17.50±0.15

17.60±0.15

Heat Treatment

Sintering

Sintering

Sintering

Sintering

Tensile Strength  (MPa)

900-1000

900-1000

900-1100

900-1100

Elongation (%)

18-29

17-27

16-26

16-24

Hardness (HRC)

24-28

25-29

25-29

26-30

AMS-T-21014

Class 3

Class 3

Class 4

Composition

95W3Ni2Fe

96W3Ni1Fe

97W2Ni1Fe

Density (g/cm3)

18.10±0.15

18.30±0.15

18.50±0.15

Heat Treatment

Sintering

Sintering

Sintering

Tensile Strength  (MPa)

920-1100

920-1100

920-1100

Elongation (%)

10-22

8-22

6-13

Hardness (HRC)

27-32

28-34

28-36

W-base high proportion alloy is a kind of matrix for tungsten content is 85-99% (W), and add a Ni, Fe, Cu, Co, Mo, Cr alloy elements, its density is as high as 16.8 to 18.8 g/cm3

Advantages

• Heavy Density
• Free cutting processing
• Excellent mechanical performance
• High elastic modulus
• Can effectively absorb xrays and gamma rays 
• (for the absorption of x rays, and gamma rays than lead high about 30% - 30%) 
• no harm to environment and health

Uses

• Radiation shielding
• A piece of balancing
• High voltage, contact
• Resistance welding electrodes