PRODUCT DISPLAY |
THZ408 |
Pure Nickel Cast Iron Electrode GB/T 10044 EZNiFe-1 AWS ENiFe-CI JIS DFCNiFe |
APPLICATIONS:
It is suitable for the welding of high-strength gray iron and nodular cast iron, such as cylinder, engine block, gear box,etc..
CHARACTERISTICS:
THZ408 is the cast iron electrode with nickel iron alloy core and strong reduction of graphite coating . It can be used in AC and DC dual purpose, has stable arc,and is easy to operate. The electrode has the characteristics of high strength, good plasticity, low linear expansion coefficient and so on. The crack resistance for grey cast iron is as much as that for THZ308, while the crack resistance for nodular cast iron is more than THZ308. For cast iron with higher phosphorus (0.2%P), it also has a good results and its tocutting performance is lower than THZ308 and THZ508 slightly. THZ408 is used in the welding of gray iron and nodular cast iron for room
ATTENTION:
1 Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 Use small current for welding as far as possible.
3 It can eliminate the welding stress and avoid the crack by the hammer.
Chemical Composition of the deposited metal(the mass fraction): %
Elements |
C |
Si |
Mn |
S |
Fe |
Ni |
Cu |
Al |
The mass of other elements |
Standard value |
≤ 2.0 |
≤ 4.0 |
≤ 2.5 |
≤0.03 |
margin |
45- 60 |
≤ 2.5 |
≤ 1.0 |
≤ 1.0 |
Welding reference current(AC,DC+)
Electrode diameter(mm) |
3.2 |
4.0 |
5.0 |
Welding current(A) |
90-110 |
120-150 |
160-190 |
THZ208
Steel Cored Gray Cast Iron Electrode GB/T 10044 EZC DFCC1 JIS
Application: welding up the defects of gray iron castings.
Features: THZ208 is the cast iron electrode with a low-carbon steel core and strong graphite type coating. It can be used in AC and DC dual purpose and has a low price. The welding seam can be changed into gray cast iron when it is cold slowly. But it has a poor anti cracking performance.
Precautions:
1 Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 The defects in small thin-wall castings with little stiffness may not be preheated weld repairs, while the general welding should be preheated to 400±10℃, kept welding heat preservation, and slow cooling, then the welding repair may be able to carry out cutting processing.
3 This electrodeb should not used to important casting structures that withstand stresses and shocks.
APPLICATIONS:
It is suitable for the welding of thin pieces of cast iron welding and machining surfaces, such as cylinder heads, important gray cast iron engine blocks, gear boxes, and Machine Tool and so on.
CHARACTERISTICS:
THZ308 is pure nickel welding core, strong reduction of graphite type coating iron rod. It can be used in AC and DC dual purpose and is easy to operate. When welding, it is not necessary for weldment to preheat. It has good crack resistance and processability.
ATTENTION:
1 Before welding, the electrodes need to be baked for 1 hour with the temperature of 150±10℃ before using.
2 It can eliminate welding stress and avoid crack by hammering the welding seam.
3. In order to reduce the impurity elements in the base metal penetration weld, narrow white band width, improve crack resistance and processing properties, it should use small current welding in cast iron cold welding.
PRODUCT APPLICATION |
Some of our products have been applied to overseas key projects.
Electrode, SAW wire and flux of 600MPa Grade & 800MPa Grade
applied to hydro steel at Laos pumped storage power station
E6010 cellulose electrode Applied to the Ghana TEMA pipeline project in Africa successfully. It breaks the monopoly of Bohler cellulose electrode and won the bidding of oil pipeline Ghana tank project
RELATED PRODUCTS |
Welding Wire | Flux Cored Welding Wire |
MORE >> | MORE >> |
ABOUT US |
We are the professional and perfect partner
of yoursin welding consumables.
F A Q |
Q: what is delivery time / lead time ?
A: 30 days
Q: what is your minimum order ?
A: 5000kgs
Q: what is your payment term ?
A: 1- 30% down payment for order confirmation, 70% before shipment.
2- 100% at sight LC
Q: can we visit your factory ?
A: yes you can at your free time.