Main Raw Materials | Polyester | Method | Spray | |||
Appearance | Powder | Substrate | Aluminium,Steel,Stainless Steel | |||
Level | Finish Coat | Formation Mechanism | Conversion Type | |||
Components | Film Forming Matters | Curing | 200℃*10mins | |||
Expiration Date | 1 year (below 30℃) | Trademark | ICK(or OEM) | |||
Transport Package | 25kg/carton | HS Code | 3907910000 | |||
CUPPING TEST | EN ISO 1520 | PASSED 5MM INDENTATION WITHOUT CRACKING | ||||
FLEXIBILITY | EN ISO 1519 | PASSED 5MM CYLINDRICAL MANDREL BEND TEST | ||||
WITHOUT CRACKING | ||||||
IMPACTRES RISTANCE | ASTMD 2794 | PASSED 23 INCH-PONDS WITHOUT CRACKING | ||||
ACETIC ACID SALT SPRAY RESISTANCE | EN ISO 9227 | MAXIMUM 16MM² INFILTRATION OVER A SCRATCH LENGTH OF 10 CM | ||||
AFTER 1,000HOURS ANY UNILATERAL PENETRATION SHALL NOT EXCEED 4MM | ||||||
ACCELERATEDWEALTHERING | EN ISO 16474-3 | 550±20W/M²(290-800NM) TEMPERATURE 65±5°C | ||||
SPECIAL UV FILTER(290NM) STAY IN 18 MINUTES FOR MOIST MEDIUM AND | ||||||
102 MINUTES FOR THE DRY MEDIUM AROUND AFTER 1,000 HOURS IRRADIATION | ||||||
NATURAL WEATHERING TEST | EN 1SO 2810 | NOCHALKING EXCELLENT GLOSS RETENTION AND COLOUR | ||||
STABILITY AFTER 12 MONTHS | ||||||
HUMIDITY RESISTANCE | EN 1SO 6270-2 | EXPOSURE (ANGLE OF 5° TO SOUTH ) NO INTILTRATION EXCEEDING | ||||
1MM BOTH SIDES OF THE SCRATCH AFTER 1,000HOURS |