RPEH-405 Modified Epoxy Anticorrosive Primer Coating Paint For Deck Ship Marine Industry
A Video of Marine Paint Project Construction.
RPEH-405 High-Build Modified Epoxy Anticorrosive Primer (Iron Red) | ||||
Uses | As maintenance antirust primer for newly-built ships or old ships. | |||
Color | Iron red | |||
Application conditions | Airless spray | Recommended | ||
Nozzle orifice | 0.4~0.5mm | |||
Nozzle pressure | 100~150kg/cm² | |||
Thinning ratio | 0~10% .by weight | |||
May be applied by spray, brush, or roller. | ||||
Thinner | FXH-4 Epoxy Thinner | |||
Mixing ratio | Two components | base/curing agent=8/1 by weight | ||
Pot life | Temperature | 10°C | 20°C | 30°C |
Pot life | 10hrs | 8hrs | 6hrs | |
Film thickness | Dry film thickness 100μm/coat & Wet film thickness:185μm/coat | |||
Solid content | 74.2% | |||
Specific gravity | 1.45 | |||
Coverage rate | Theoretical | 0.21kg/m2/100μm 0.148L/m2/100μm | ||
Actual: depending on the surface treatment, environment and application methods | ||||
Dry time | Temperature | 10°C | 20°C | 30°C |
Dry to touch | 2hrs | 1.5hrs | 1hrs | |
Dry to handle | 14hrs | 10hrs | 8hrs | |
Coating interval | Min. | 14hrs | 10hrs | 8hrs |
Max. | — | — | — | |
Shelf life | 12 months | |||
Packing | A kit 22.5kg contains Part A 20kg and Part B2.5kg | |||
Surface preparation | 1.Remove salts and other water soluble contaminants with fresh water. 2.Remove oil in accordance with the solvent cleaning standard SSPC-SP1. 3.Remove rust and scale by sand blasting to ISO Sa 2.5 (SSPC-SP10). 4.Remove the contaminants like dust with high pressure blower. 5.Confirm the surface clean and dry before working. | |||
Coating system | Steel: Bare steel | |||
Top coat: refer to our coating system |