Titanium Substrate | Grade | N | C | H | Fe | O | Ti | ||||||
1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | bal | |||||||
2 | 0.03 | 0.05 | 0.015 | 0.3 | 0.25 | bal | |||||||
Regular Coating | Platinum:0.5um/1um; Mixed Iridium and Platinum:0.5um/1um; Mixed Ruthenium and Iridium:6-8um; Mixed Iridium and Tantalum:6-8um. | ||||||||||||
Characteristics | Coating: Mixed Ruthenium and Iridium; Chlorine evolution potential: <1.13V; Polarizability: ≤40mv; Accelerated life: ≥3000min under current density 1000A/m2; Anode strengthening weightlessness: ≤10mg; Suitable working environment: Solution contains Cl-, PH<=7 | ||||||||||||
Coating contents & life span | 8 grams/m2: >6,000 hours; 10 grams/m2: > 8,000 hours; 12 grams/m2: >10,000 hours; 15 grams/m2: >12,000 hours; 20 grams/m2: >15,000 hours | ||||||||||||
Working parameters | Current density: <600A/m2; Temperature: 40-60°C; Chlorine concentration: About 30~50grams/liter; Polarity reversal: suitable; Reversal frequency: 2-4 hours | ||||||||||||
Regular sizes | 63.5*150mm, 13pcs/set; 64*110mm, 7pcs/set; 80*120mm, 1pcs/set; 30*183mm, 7pcs/set; 80*185mm, 7pcs/set | ||||||||||||
Applications | 1.Water ionizer or water electrolysis a. Making alkaline and acidic water 2.Waste water treatment a.Organic sewage treatment, b. Chemical sewage treatment, c. Pesticide sewage treatment, d. Drinking water disinfection, e. Bleaching & dyeing, f. Swimming pool g. Hospital sewage treatment, h. Food industry disinfection etc. 3.Sodium Hypochlorite Generator & Chlorinator a. Swimming pool water treatment b. Water sterilization & water purification, 4.Sea water electrolysis or Electrodialysis a. Desalination, b. Material recycling in the waste water, c. Paper making, *Chemical, medical industry, d. Light industry, *Metallurgy, e. Making fresh water, etc. 5.Chlor-Alkali Industry 6.Electroplating a. Electrolating Au,Cr,Zn,Cu.etc 7.MMO Cathodic Protection |