Typical properties | |||
Characteristics(1) | Test Method | Unit | Value |
Physical | |||
Density | ASTM D1505 | g/㎤ | 0.9 |
MFR(230℃,2.16Kg) | ASTM D1238 | g/10min | 60 |
Mechanical(2) | |||
Tensile Strength at Yield(3) | ASTM D638(3) | MPa | 31 |
Elongation at Break(3) | ASTM D638(3) | % | <50 |
Flexural Modulus(4) | ASTM D790(4) | MPa | 1900 |
Izod Impact Strength (Notched, 23℃) | ASTM D256 | J/m | 45 |
Izod Impact Strength (Notched, -20℃) | 30 | ||
Hardness(R-scale) | ASTM D785 | - | 105 |
Thermal | |||
Vicat Softening point (1kgf) | ASTM D1525 | ℃ | 152 |
Heat Deflection Temperature (4.6kgf/cm2) | ASTM D648 | ℃ | 135 |
IZOD Impact Strength, 6.4mm | ASTM D256 | ||
(Notched) | 23℃ | kg·cm/cm | |
-30℃ | kg·cm/cm | ||
IZOD Impact Strength, 3.2mm | ASTM D256 | ||
(Notched) | 23℃ | kg·cm/cm | |
-30℃ | kg·cm/cm | ||
Rockwell Hardness | R-Scale | ASTM D785 | - |
Thermal | |||
Heat Deflection Temperature, 6.4mm | ASTM D648 | ||
(Unannealed) | 18.6kg | ℃ | |
4.6kg | ℃ | ||
Vicat Softening Temperature | ASTM D1525 | ||
5kg, 50℃/h | ℃ | ||
Flammability | UL94 | ||
1.5mm | class | ||
3.0mm | class | ||
Relative Temperature Index | UL 746B | ||
Electrical | ℃ | ||
Mechanical with Impact | ℃ | ||
Mechanical without Impact | ℃ |