1.PC Polycarbonate granule
2.Free sample
3.Injection grade,extrusion grade,blow film grade
4.Widely used in engineering
PC- Polycarbonate
Specific gravity: 1.18-1.20g/cm3
Moulding shrinkage: 0.5-0.8%
Moulding temperature: 230-320C
Drying condition: 8 hours under 110-120C
Usage temperature: -60~120C
Properties: High impact strength, shape stable, colourless, transparent, easy dying, electric insulation, corrosion resistance, wear resistance are good. However, poor self-lubricating, with tendency to stress cracking, high temperature easily hydrolyzed, poor compatibility with other resins. PC is suitable for making instrument small parts, insulating and transparent parts and impact-resistant parts.
PC usually is made into products by injection molding, extrusion, coining, blow molding, thermoforming, printing, adhesive, coating and machining, the most important processing method is injection molding.
PC Usage:
1. PC is made into large bulb shade, protective glass, the right and left eyepiece tube of optical instruments. Also, it is used as the transparent materials in plane.
2. PC is good insulation, made into insulated connector, coil frame, tube socket, insulating sleeve, telephone housing and parts, miner's lamp battery shell. Also, it is used to make fine parts of communication equipment, such as CD-ROM, telephone, computer, video recorder, telephone switches, signal relay. The PC film is used for capacitors, insulation foreskin, recorder, color video tape. etc
3. Machinery and equipment-PC is suitable for gear, rack, worm, bearings, cams, bolts, crank, ratchet, also suitable for machinery and equipment housings, covers and frames.
4. PC can be made into cap, tube, bottle and dental equipment, drug containers and surgical instruments. Even be used as an artificial kidney, artificial lung and other artificial organs.
5. For architectural, PC can be made into Double-wall hollow bars, glass of greenhouse. For textile industry, PC is suitable for making bobbin, textile machine bearing. For daily, PC is good material can be made into tableware, toys and models.
Specification:
Test items | Test methods | test conditions | Unit | Glass fiber reinfored | Glass fiber reinforved& | Flame retardant type | |||||
Type | F;ame retardant Type | ||||||||||
PC01 | PC01 | PC01 | PC03 | PC03 | PC | ||||||
G10 | G20 | G30 | G10 | G30 | |||||||
Physical | Proportion | D-792 | 23oC | - | 1.27 | 1.31 | 1.43 | 1.28 | 1.44 | ||
Properties | |||||||||||
Molding shrinkage | D-955 | 23oC | % | 0.2-0.4 | 0.1-0.3 | 0.1-0.3 | 0.3-0.5 | 0.1-0.3 | |||
Mechanical properties | Tensile steength | D-638 | RH50.23oC | Mpa | 78 | 103 | 120 | 71 | 115 | ≥58.8 | |
Elongatin at break | D-638 | RH50.23oC | % | 5 | 4 | 3 | 4.8 | 3 | ≥70 | ||
Flexural strength | D-790 | RH50.23oC | Mpa | 127 | 157 | 186 | 121 | 150 | ≥93 | ||
Simple bean | D-648 | D-256 | RH50.23oC | KJ/M2 | 97 | 127 | 145 | 91 | 135 | ≥45- | |
Thermal | Heat distortion | D-648 | 1.82Mpa | oC | 142 | 146 | 149 | 143 | 149 | ≥126 | |
performane | temperature | ||||||||||
Flame-retardant | UL-94 | 0.8-3.2MM | 94V-2 | 94V-2 | 94V-2 | 94V-0 | 94V-0 | ||||
Electrical | Volume resistivity | D-257 | RH50.23oC | Ω.m | 1x1016 | 1x1016 | 1x1016 | 1x1016 | 1x1016 | ≥5x1015 | |
properties | |||||||||||
Dielectric strength | D149 | RH50.23oC | KV/MM | 30 | 30 | 30 | 30 | 30 | ≥16 |
If you are interested in our products,please feel free to contact with us.