Product name | HDPE Granules |
Type | Plastic Raw Materials Granules |
Color | Transparent and other colors |
Shape | Pellet - Granules |
Application | Packaging of all kinds of articles |
Density | 0.924 g/cm3 |
MFR | 0.6 - 0.8 G/10 Min |
Melting point | 110~115℃ |
Processing | 150~210℃ |
Item | Test condition | Test Method | Value | Unit |
Density | ISO 1183 | 0.944-0.955 | g/cm3 | |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield | ISO 527-2 | 22 | MPa | |
Elongation at break | ISO 527-2 | >350 | % | |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
VICAT | ASTM D-1525 | 126 | °C |
Item | Test Condition | Test Method | Value | Unit |
Density | ISO 1183 | 0.950~0.955 | g/cm3 | |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield | ISO 527-2 | 24 | MPa | |
Elongation at break | ISO 527-2 | >600 | % |
Item | Test Condition | Test Method | Value | Unit |
MFR | 190°C/2.16kg | ASTM D-1238 | 20 | g/10min |
Density | --- | ASTM D-792 | 0.954 | g/cm3 |
Tensile strength at yiled | --- | ASTM D-638 | 28 | MPa |
Elongation at break | --- | ASTM D-638 | 250 | % |
Impact tensile strength | --- | ASTM D-1822 | 42 | kJ/m2 |
ESCR | --- | ASTM D-1693 | 3 | --- |
VACIT | --- | ASTM D-1525 | 127 | °C |
Property | Unit | Typical Value | |
Mass density | g/cm3 | 0.941-0.959 | |
Melt flow Rate(190 centidegree /2.16kg) | g/10min | ≤1.0 | |
Tensile yield strength | MPa | ≥19.0 | |
Flexural modulus | Mpa | ≥965 | |
Elongation@ break | % | ≥400 | |
Impact Embrittlement temperature | Centidegree | MAX -118 | |
Dielectric Constant | 100KHZ 1MHZ | 2.32 2.31 | |
Loss Tangent | 100KHZ 1MHZ | MAX 0.0001 MAX 0.0001 | |
Volume resistivity | OHM-CM | MIN 1x10 15 | |
Application | Mainly used for the production of high toughness of the telephone,cable insulation material |