NEITABOND marble aluminum composite panel vividly imitate the subtle texture of marble and easy to clean surface,can be directly wiped with water once dust contamination,with recyclable,anti corrosion features,it is belong tp green and environmentlly-friendly building materials,has long service life and wear resistance.
Aluminum Alloy | AA1100 ,AA3003,AA5005 |
Aluminum Skin | 0.08mm,0.10mm,0.12mm,0.15mm,0.18mm,0.21mm, 0.25mm,0.30mm,0.35mm,0.40mm,0.45mm,0.50mm |
Panel Thickness | 3mm,4mm |
Panel Width | 1220mm |
Panel Length | 2440mm,3050mm,4050mm,4880mm,5000mm ect |
Surface Treat | wood texture |
Customers Size | ACCEPTED |
Glossy | 20%-40% |
PVDF painting unbreakable surface interiorwall cladding granite texture ACP
wall cladding granite texture ACP
Linyi Xingda Aluminum-Plastic Decoration Materials Co., Ltd. has seven world-level advanced multifunctional fully automated production lines, which assure annual production capacity of 6,000,000 square meters and the max width reach 1550mm. We choose the best quality of raw materials for the Production of products.
1)Complete Product Series with competitive price
2)Prompt lead time:10-15 working days after deposite.31500sq.m per day with 7high speed production
3)Complete inspection system
4)Official Cettificates:ISO by TUV,BV,ASTM E84
5)Complete After-sales service system
6)Direct factory,17 years experience:Neitabond,since 2003
7)Free OEM Service
Description | Test standard | Polyester |
Thickness of coating | Polyester paint>=16um | 16um to 18um |
Coating flexibility (T-bend) | Polyester paint≥3T | 3T |
Color different | ΔE<=2.0(follow color sample) | ΔE<=2.0 |
Pencil hardness | >=HB | >=2H |
Chemical resistance | 2%HCI or 2% NaOH test in 24 hours -No change | No change |
Coating adhesion | >=1grade for 10*10mm2 gridding test | 1grade |
Resist solvent | 100times with Dimethy benzene without change | No change |
Boiling water resistance | 2 hours without change | No change |
Peeling strength/stripping strength | Average >=5N/mm of 180oc peel off for panel with 0.21mm alu.skin | 5N/mm |
Impact test for paint | 20KG.cm impact-paint no split for panel | No split |
Abrasion resistance (L/Mil) | NIL | NIL |
Temperature resistance | -40ºC to +80ºC temperature without change of color difference and paint peel off,peeling strength average dropprate <=10% | Change of glossy only,no paint Peel off |
Coefficient of linear Thermal Expansion | 100ºC temperature difference | 2.4mm/m |
Detergent resistance (3%) | ASTM D2248 | No change |
Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | No change |
Salt spray resistance (3000hrs,5% salt) | ASTM B117 | No change |
Resistance to Staining | 600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference <=4.0 | No change |
♦ Why choose us--Linyi Xingda Neitabond?
High Quality
As one of main supplier of ACP, control the material from each small part and provide a high-quality products to our client.
♦ What material of our Aluminium Composite Panel?
Aluminium Composite Panels are made by two sheets of decorative aluminium Coil and a PE core ,the stricture is like sandwich .
♦ If the color can be customized?
The color can be customized, the MOQ is 1000sqm
♦ when we can ship goods after place an order?
Delivery time is about 7-15 days as per order qty.
♦ How we can received a sample and what is our sample policy?
We can provide free sample to testing or evaluating. The shipping charges by courier should be bear by customer.But this shipping cost can be deducted from official order.
♦ What is our payment Term?
30%T/T deposite in advance,the balance paid against copy of shipping documents is our standard payment term.L/C at sight is also o