BRAND: | HUAFON | GRADE: | EP626F | ||
MATERIAL: | PA66 | ||||
FEATURES: | 1. HIGH STRENGTH | 2. GOOD FLOW | 3. SURFACE LUBRICITY | ||
COLOR: | CUSTOMIZED | ||||
FORM: | PELLETS | ||||
METHOD: | INJECTION MOLDING |
Properties | Test Condition | Test Method | Unit | Typical Value |
Physical | ||||
Relative Viscosity | QB | - | 2.62±0.05 | |
Melt Flow Rate | 275℃/2.16kg | ISO1133 | g/10min | 90 |
Mechanical
| ||||
Tensile Strength | ISO 527 | mpa | 76 | |
Elongation at break | ISO 527 | % | 55 | |
Flexural Strength | ISO 178 | mpa | 99 | |
Flexural Modulus | ISO 178 | mpa | 2,704 | |
Charpy Impact | Notched, 23℃ | ISO 179 | kj/m² | 6.1 |
Thermal
| ||||
Heat Deflection Temperature | 1.80Mpa | ISO 75 | ℃ | 66 |
Melting Point | 10℃/min | ASTM D3418 | ℃ | 262 |
Vicat Softening Temperature | ISO 306 | ℃ | - |