PA6 DGK-GR30L High strength glass fiber reinforced 30% water pump water valve automotive accessories plastic granules
Product Features: High strength, high rigidity, good heat resistance, low water absorption and good processing
Performance: Among them, there is no floating fiber reinforced nylon 6 grade, and the surface gloss is good.
Product Application: Used in various machine fan blades, electrical housings, sports equipment, power tools, etc
PA6 E0715
Product Description | Applications | ||||||||
·15%6 15% glass fiber reinforced PA6 | · Injection molding | ||||||||
· Excellent heat stability | · Good mechanical properties balance | ||||||||
Properties | Test Method | Test Condition | Unit | Typical Values | |||||
Physical properties | |||||||||
Specific Gravity | ISO 1183 | 23ºC | g/cm3 | 1.24 | |||||
Ash | ISO 3451 | 800ºC,30min | % | 15 | |||||
Mechanical properties | |||||||||
Tensile Strength | ISO 527 | 50mm/min | MPa | 120 | |||||
Elongation at Break | ISO 527 | 50mm/min | % | 3 | |||||
Flexural Modulus | ISO 178 | 2mm/min | MPa | 5300 | |||||
Charpy Notched Impact Strength | ISO 179-1eA | 23ºC | kJ/m2 | 7 | |||||
Charpy Unotched Impact Strength | ISO 179-1eU | 23ºC | kJ/m2 | 45 | |||||
Thermal properties | |||||||||
Heat deflection temperature | ISO 75 | 1.80MPa | C | 185 | |||||
Melting Point | DSC | - | C | 222 | |||||
Other properties | |||||||||
Flammability | TL1010 | - | mm/min | 39 | |||||
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to use the material, please consult with TOPO Co.LTD. | |||||||||
Processing Conditions | Range | ||||||||
Melt Temperature | 240-270ºC | ||||||||
Mold Temperature | 50-80ºC | ||||||||
Pre-Dry needed | 100ºC, 4-8h |