Item | Test Result | Item | Test Result |
Transmittance% | 94 | Tensile Strain at Break, Mpa | 5 |
Rockwell Hardness(M) | 97 | Modulus of elasticity in tension, Mpa | 3.03 |
Vicat Softening Temperature(1.8MPA) | 101 | Rockwell Hardness(R) | 124 |
Coefficient of Thermal Expansion ℃-1 | 7.0*10-5 | Resistance to crazing in solvent | No crazing |
Dimensional Stability(shrinkage) % | 1.9 | Charpy Non-notch Impact Strength KJ/M2 | 21.9(C) |
Tensile strength, Mpa | 74.7 |
Code | Size with rubber edge | Size after cut edge |
Q | 1250*1850mm | 1210*1820mm |
L0 | 1250*2450mm(Include Frosted) | 1210*2420mm(Include Frosted) |
L1 | 1270*2490mm | 1220*2440mm |
L2 | 1310*2530mm | 1270*2490mm |
L3 | 1350*2570mm | 1310*2530mm |
Y | 1650*2600mm | 1610*2660mm |
N | 1550*3050mm | 1510*3020mm |
M | 2050*3050mm(Include Frosted) | 2010*3010mm(Include Frosted) |