Typical value at 23℃ | Unit | Test standard | B1GF6 | |||
Properties | ||||||
Symbol | - | ISO 1043 | PBT+30%GF | |||
Specific gravity | cm3/g | ISO 1183 | 1.52 | |||
Viscosity | ml/g | ISO 307 | ||||
Water absorption,at 23℃ water saturated | % | ISO 62 | ||||
Moistrue absorption | % | ISO 62 | ||||
Melting point,DSC | ℃ | DIN 53 765 | ||||
Melt volume flow rate, MFR 260/5 | cm3/10min | ISO 1133 | 12 | |||
Melt temperature range,injection molding/extrusion | ℃ | 250-270 | ||||
Mold temperature range,injection molding | ℃ | 80 | ||||
Tensile modulus of elasticity | Mpa | ISO 527-1/-2 | 9300 | |||
Tensile strength, break | Mpa | ISO 527-1/-2 | 140 | |||
Tensile elongation, break | % | ISO 527-1/-2 | 3 | |||
Bending modulus | Mpa | ISO 178 | 9000 | |||
Bending strength | Mpa | ISO 178 | 200 | |||
CHARPY impact strength +23℃ | KJ/㎡ | ISO 179/IeU | 55 | |||
Notched izod impact strength +23℃ | KJ/㎡ | ISO 180/A | ||||
HDT 1.8Mpa under load | ℃ | ISO 75-1/-2 | 205 | |||
HDT, 0.45 Mpa under load | ℃ | ISO 75-1/-2 | ||||
CLTE, transverse and longitudinal | 10-4/K | ISO 11359-1/-2 | ||||
Heat conductivity | W/(m.K) | DIN 52 612 | ||||
Specific heat volume | J/(kg•k) | |||||
According UL standard | Class | UL94 | ||||
Dielectric factor at 1 MHZ | IEC 60250 | |||||
Dissipation factor at 1 MHZ | 10-4 | IEC 60250 | ||||
Volume resistivity | Ω•m | IEC 60093 | ||||
Surface resistivity | Ω | IEC 60093 | ||||
CTI | IEC 60112 | |||||
Typical value These data should only be used as classical values. Unless expressly agreed in writing,can not be identified as the index or guarantee value of the material. The performance of the product is affected to some extent by mold/head design, processing conditions and coloring. Unless specified, all data are derived from tests performed on standard samples at room temperature. |