Properties | Test Condition | Test Method | Unit | Typical Value | ||||
Physical | ||||||||
Specific Gravity | ASTM D792 | - | 1.14 | |||||
Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.5~0.8 | |||||
Melt Flow Rate | 250℃/2.16kg | ASTM D1238 | g/10min | 6 | ||||
Mechanical | ||||||||
Tensile Strength, 3.2mm | ASTM D638 | |||||||
@ Yield | 50mm/min | kg/cm2 | 570 | |||||
Tensile Elongation, 3.2mm | ASTM D638 | |||||||
@ Yield | 50mm/min | % | ||||||
@ Break | 50mm/min | % | >100 | |||||
Flexural Strength, 3.2mm | 10mm/min | ASTM D790 | kg/cm2 | 920 | ||||
Flexural Modulus, 3.2mm | 10mm/min | ASTM D790 | kg/cm2 | 23,000 | ||||
IZOD Impact Strength, 3.2mm | ASTM D256 | |||||||
(Notched) | 23℃ | kg·cm/cm | 58 | |||||
-30℃ | kg·cm/cm | 30 | ||||||
Rockwell Hardness | R-Scale | ASTM D785 | - | 114 | ||||
Thermal | ||||||||
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||||||
(Unannealed) | 18.6kg | ℃ | 114 | |||||
4.6kg | ℃ | |||||||
Vicat Softening Temperature | ASTM D1525 | |||||||
5kg, 50℃/h | ℃ | |||||||
Ball Pressure Temperature | IEC 60695-10-2 | ℃ | ||||||
Burning Rate, 3.2mm | FMVSS 302 | mm | ||||||
Flammability | UL94 | |||||||
0.8mm | class | |||||||
1.6mm | class | |||||||
2.5mm | class | |||||||
3.0mm | class | |||||||
Relative Temperature Index | UL 746B | |||||||
Electrical | ℃ | |||||||
Mechanical with Impact | ℃ | |||||||
Mechanical without Impact | ℃ |