BRAND: | LG CHEM | GRADE: | LUPOY GN8010F |
MATERIAL: | SILICON PC | ||
FEATURES: | 1. GENERAL PURPOSE | 2. HIGHT IMPACT | |
APPLICATIONS: | 1. IT&OA | 2. E&E HOUSING AND COMPONENTS | |
FORM: | PELLETS | ||
PROCESSING METHOD: | INJECTION MOLDING |
Properties | Test Condition | Test Method | Unit | Typical Value |
Physical | ||||
Specific Gravity | ASTM D792 | - | 1.2 | |
Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.5~0.7 | |
Melt Flow Rate | 300℃/1.2kg | ASTM D1238 | g/10min | 11 |
Mechanical | ||||
Tensile Strength, 3.2mm | ASTM D638 | |||
@ Yield | 5mm/min | kg/cm2 | 610 | |
Tensile Elongation, 3.2mm | ASTM D638 | |||
@ Yield | 5mm/min | % | ||
@ Break | 5mm/min | % | 80 | |
Flexural Strength, 3.2mm | 10mm/min | ASTM D790 | kg/cm2 | 980 |
Flexural Modulus, 3.2mm | 10mm/min | ASTM D790 | kg/cm2 | 23,000 |
IZOD Impact Strength, 3.2mm | ASTM D256 | |||
(Notched) | 23℃ | kg·cm/cm | 80 | |
-30℃ | kg·cm/cm | 60 | ||
Thermal | ||||
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
(Unannealed) | 18.6kg | ℃ | 125 | |
4.6kg | ℃ | |||
Vicat Softening Temperature | ASTM D1525 | |||
5kg, 50℃/h | ℃ | |||
Flammability | UL94 | |||
1.5mm | class | V-0 | ||
3.0mm | class | V-0 | ||
Relative Temperature Index | UL 746B | |||
Electrical | ℃ | 80 | ||
Mechanical with Impact | ℃ | 80 | ||
Mechanical without Impact | ℃ | 80 |