BRAND: | LG CHEM | GRADE: | LUPOY EF1006FM |
FEATURES: | 1. HALOGEN FREE FLAME RETARDANT | 2. HIGH HEAT RESISTANCE | |
APPEARANCE: | 1. IT/OA HOUSING AND COMPONENTS | ||
FORM: | PELLETS | ||
PROCESSING METHOD: | INJECTION MOLDING |
Properties | Test Condition | Test Method | Unit | Typical Value | ||||
Physical | ||||||||
Specific Gravity | ASTM D792 | - | 1.21 | |||||
Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.5~0.7 | |||||
Melt Flow Rate | 220℃/10kg | ASTM D1238 | g/10min | 12 | ||||
Mechanical | ||||||||
Tensile Strength, 3.2mm | ASTM D638 | kg/cm2 | ||||||
@ Yield | 50mm/min | 630 | ||||||
Tensile Elongation, 3.2mm | ASTM D638 | |||||||
@ Yield | 50mm/min | % | ||||||
@ Break | 50mm/min | % | 100 | |||||
Flexural Strength, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 970 | ||||
Flexural Modulus, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 23,000 | ||||
IZOD Impact Strength, 3.2mm | ASTM D256 | |||||||
(Notched) | 23℃ | kg·cm/cm | 70 | |||||
-30℃ | kg·cm/cm | |||||||
Rockwell Hardness | R-Scale | ASTM D785 | - | 118 | ||||
Thermal | ||||||||
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||||||
(Unannealed) | 18.6kg | ℃ | 130 | |||||
4.6kg | ℃ | |||||||
Vicat Softening Temperature | ASTM D1525 | |||||||
5kg, 50℃/h | ℃ | 140 | ||||||
1kg, 120℃/h | ℃ | |||||||
Flammability | UL94 | |||||||
1.0mm | class | V-0 | ||||||
1.5mm | class | V-0 | ||||||
1.7mm | class | V-0,5VB | ||||||
3.0mm | class | V-0,5VA | ||||||
Relative Temperature Index | UL 746B | |||||||
Electrical | ℃ | 125 | ||||||
Mechanical with Impact | ℃ | 120 | ||||||
Mechanical without Impact | ℃ | 125 |