KGT TITANIUM DIOXIDE R-960 titanium dioxide pharmaceutical grade

Company profile:

We are pround to inform that we successful passed all the assessment by Bureau Veritas!

Product Description

Figure 1.   Optical Properties 

R960 is a rutile titanium dioxide pigment manufactured by the chloride process. It is excellent for exterior plastic applications that require outstanding chalking resistance and  gloss, tint, and physical property retention. The grade is a fne, dry, white powder with typical properties as shown in Table 1. 

Suggestions for Use 

KGT R960 is designed primarily for exterior color durable  Low   Cream applications. 

The surface treatment of R960 minimizes potential  reaction with polymer resins and additives, while continuing to  provide the high level of UV radiation protection associated with rutile titanium dioxide. 

In tinted exterior applications, the lower  opacity strength of R960 actually minimizes the total colorant  cost at the desired level of UV protection. 

Rutile titanium dioxide is an effcient UV radiation protector for  plastic applications because it strongly absorbs radiation below  380 nm. Rutile titanium dioxide, in the presence of water and  oxygen, may then act as a photocatalytic agent. TiPureoxygen, may then act as a photocatalytic agent. 

 KGT R-960  is surface coated with silica to minimize this photocatalytic  potential. 

An additional alumina treatment improves dry bulk  conveying and dispersibility. 

Table 2 

General Properties 

R960 provides maximum surface retention while still providing  effcient UV radiation protection. Figures 2 and 3  demonstrate  the improved gloss retention of R960 in plastics, compared to  grades R-101 and R-103. 

Figure 2.   Gloss Retention of Polypropylene, Xenon Exposure 

The surface treatments used to optimize R960 outdoor  performance are hygroscopic. Moisture absorbed during shipping  and storage can affect flm integrity at very high TiO2  loadings  and temperatures. As Figure 4  shows, R960 must be evaluated  carefully for flm applications. For applications requiring less  moisture, R-105 is recommended. 

Figure 4.   Lacing Resistance versus Temperature, 

Figure 3.   Gloss Retention of PVC, Florida Exposure 45° South 

Shipping Containers 

R960 rutile titanium dioxide is available in a range of packaging to  meet your needs: 

• 50 lb multi-ply paper bags 

• 25 kg multi-ply paper bags 

• 1 metric ton (1,000 kg) fexible intermediate bulk containers 

•4 phr TiO2  in lead stabilized window compound 

For further information about this grade or to request a sample,  please see the Titanium Technologies web site.