Low thermal conductivity;Good thermal insulation performance
Refractory category allow direct contact of fire,suitable for various atmosphere
Good integrity with furnace lining,long service life,easy operation,could be shaped freely
Low iron content;Good eroding resistance
Steel Furnace;Iron making furnace;Glass kiln;Ceramic tunnel kiln;Cement kiln;Lime kilns;Suspended roofs;Reheating furnaces;Blast furnaces;Coke ovens;Insulation for glass tanks;Preheat zones and cyclones of rotary cement kilns ;Carbon bake furnaces in the aluminium industry;Furnaces of metallurgy industry heat treatment furnace;Furnaces of chemical industry and construction industry.;Tunnel kiln car,shuttle kiln car
SIZE:230*114*76MM 230*114*65MM 230*114*65/45MM 230*114*65/50MM
Other size depend on the users.
The specification is for the standard size.
Item | Sk-32 |
AI2O3(%) | 35 |
Fe2O3 (%) | 3 |
Refractoriness (SK) | 32/ 1710℃ |
Refractorines under load, 0.2MPa, Ta, (°C) | 1300 |
Porosity(%) | 19-22 |
Bulk density (g/cm3) | 2.10-2.15 |
Cold crushing strength (Mpa) | 25-30 |
Thermal expansion at 1000℃ (%) | 0.6 |
SIZE:230*114*76MM 230*114*65MM 230*114*65/45MM 230*114*65/50MM
Other size depend on the users.
The specification is for the standard size.
Item | Sk-34 |
AI2O3(%) | 40 |
Fe2O3 (%) | 2.5 |
Refractoriness (SK) | 34/ 1750℃ |
Refractorines under load, 0.2MPa, Ta, (°C) | 1350 |
Porosity(%) | 19-23 |
Bulk density (g/cm3) | 2.15-2.20 |
Cold crushing strength (Mpa) | 30-40 |
Thermal expansion at 1000℃ (%) | 0.6 |
SIZE:230*114*76MM 230*114*65MM 230*114*65/45MM 230*114*65/50MM
Other size depend on the users.
The specification is for the standard size.
Item | Sk-36 |
AI2O3(%) | 50 |
Fe2O3 (%) | 2 |
Refractoriness (SK) | 36/ 1790 ℃ |
Refractorines under load, 0.2MPa, Ta, (°C) | 1450 |
Porosity(%) | 20-24 |
Bulk density (g/cm3) | 2.25-2.30 |
Cold crushing strength (Mpa) | 35-45 |
Thermal expansion at 1000℃ (%) | 0.3 |
SIZE:230*114*76MM 230*114*65MM 230*114*65/45MM 230*114*65/50MM
Other size depend on the users
The specification is for the standard size.
Item | Sk-37 |
AI2O3(%) | 60 |
Fe2O3 (%) | 2 |
Refractoriness (SK) | 1790 ℃ |
Refractorines under load, 0.2MPa, Ta, (°C) | 1450 |
Porosity(%) | 20-24 |
Bulk density (g/cm3) | 2.30-2.35 |
Cold crushing strength (Mpa) | 40-50 |
Thermal expansion at 1000℃ (%) | - |
SIZE:230*114*76MM 230*114*65MM 230*114*65/45MM 230*114*65/50MM
Other size depend on the users
The specification is for the standard size.
Item | SK-38 |
AI2O3(%) | 70 |
Fe2O3 (%) | 2 |
Refractoriness (SK) | 38/1800 |
Refractorines under load, 0.2MPa, Ta, (°C) | 1500 |
Porosity(%) | 21-24 |
Bulk density (g/cm3) | 2.35-2.40 |
Cold crushing strength (Mpa) | 50 |
Thermal expansion at 1000℃ (%) | - |
SIZE:230*114*76MM 230*114*65MM 230*114*65/45MM 230*114*65/50MM
Other size depend on the users
The specification is for the standard size.
Item | ||
AI2O3(%) | 75 | 80 |
Fe2O3 (%) | 2 | 2 |
Refractoriness (SK) | 1800℃ | 1800℃ |
Refractorines under load, 0.2MPa, Ta, (°C) | 1500 | 1500 |
Porosity(%) | 21-24 | 21-24 |
Bulk density (g/cm3) | 2.40-2.45 | 2.50-2.60 |
Cold crushing strength (Mpa) | 50-60 | 50-65 |
Thermal expansion at 1000℃ (%) | -- | -- |