Chemical Composition | C(%): 3.0-5.0 ,Cr(%): 25-40. |
The carbide (Cr7C3) volume fraction on the microstructure is above 50% | |
Wear Resistance | High wear resistance,30 times higher than low carbon steel and 12 times than heat treated steel |
Main Thicknesses | 10+4,10+5,10+6,10+7,10+8,10+9,10+10,10+20 12+4,12+5,12+6,12+7,12+8,12+10,12+11,12+12 14+6,14+8,14+10,16+6,16+8,16+10 18+6,18+8,18+10,20+5,20+6,20+8,20+10,20+20,30+10,40+10 Customized. |
Plate Size | Open arc welding wear plate:1400*3400mm Submerged arc welding wear plate:1400*3000mm, 1400*3500mm, 2100*3500mm. Customized. |
Chemical Content | ||||||||||||||||
Steel/Grade | C | Si | Mn | P | S | AL | Cr+Ni+Mo | Nb+V+Ti | ||||||||
NM360/AR360 | 0.10-0.30 | 0.20-0.40 | 1.00-2.00 | ≤0.015 | ≤0.003 | ≥0.20 | <0.6 | Trace Amount | ||||||||
NM400/AR400 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | ≤0.015 | ≤0.003 | ≥0.20 | <0.9 | |||||||||
NM450/AR450 | 0.10-0.40 | 0.20-0.40 | 1.00-2.00 | ≤0.015 | ≤0.003 | ≥0.20 | <1.2 | |||||||||
NM500/AR500 | 0.10-0.40 | 0.20-0.45 | 1.00-2.00 | ≤0.015 | ≤0.003 | ≥0.20 | <1.5 | |||||||||
NM550/AR550 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | ≤0.015 | ≤0.003 | ≥0.20 | <2.0 | |||||||||
NM600/AR600 | 0.10-0.50 | 0.20-0.45 | 1.00-1.50 | ≤0.015 | ≤0.003 | ≥0.20 | <2.5 |