Type | SYN-1260 | SYN-1400 | SYN-1500 | SYN-1600 | SYN-1700 | SYN-1800 | SYN-1900 | ||
Classification Temperature(℃) | 1260 | 1400 | 1500 | 1600 | 1700 | 1800 | 1900 | ||
Working Temperature(℃) | 1000 | 1200 | 1350 | 1500 | 1600 | 1700 | 1750 | ||
Color | Pure White | Pure White | Pure White | Pure White | Pure White | Pure White | Pure White | ||
Density(kg/m3) | 250-400 | 250-400 | 3 00-400 | 400 | 400 | 400-500 | 700 | ||
Thermal Conductivity(w/mk) | 0.09400℃ | 0.09 | - | - | - | - | - | - | |
600℃ | 0.12 | 0.12 | 0.12 | - | - | - | - | ||
800℃ | 0.16 | 0.15 | 0.16 | 0.14 | 0.15 | 0.17 | 0.2 | ||
1000℃ | - | 0.23 | 0.23 | 0.17 | 0.19 | 0.24 | 0.3 | ||
1200℃ | - | - | 0.25 | 0.23 | 0.27 | 0.28 | 0.33 | ||
Chemical Comsosition(%) | Al2O3 | 43 | 45 | 60 | 64 | 75 | 80 | 87 | |
Al2O3+SiO2 | 98 | 98 | 98 | 98 | 99 | 99.5 | 99.5 | ||
BaO | <0.2 | <0.2 | <0.2 | <0.1 | <0.05 | <0.05 | <0.05 | ||
Fe2O3 | <1.2 | <1.2 | <0.5 | <0.5 | <0.2 | <0.1 | <0.1 | ||
Shrinkage(%) | 1100℃*24h-3 | 1200℃*24h-2.5 | 1400℃*24h-2 | 1500℃*24h-1 | 1600℃*24h-0.5 | 1700℃*24h-0.40 | 1750℃*24h+0.1~-0.4 | ||
Combustion Loss(%) | ≤5% | ≤5% | ≤4.5% | ≤4.5% | ≤5% | ≤3.5% | ≤4% | ||
Compressive Strength(MPa) | 0.3 | 0.4 | 0.5 | 0.5 | 0.6 | 0.6 | 0.8 |