Test Method | Test Parameter | Unit | Result | |||
As Supplied-Tested at 25℃ and 50% RH | ||||||
CTM 101 | Specific Gravity | g/ml | 1.01 | |||
ASTM C603 | Extrusion Rate | ml/minute | 100 | |||
CTM 001 | Tack-free | minute | ≤1 | |||
CTM 003 | Curing Speed, average | mm/day | 2 | |||
As Cured-after 14 days at 25℃ and 50% RH | ||||||
ASTM C661 | Durometer Hardness, Shore A | Points | 30 | |||
ISO 9047 | Movement Capability | % | ±25 | |||
ISO8339 | Tensile/Modulus at,50%Elongation | MPA | 0.27 | |||
Tensile/Modulus at,100%Elongation | MPA | 0.55 | ||||
Ultimate Tensile Strength | MPA | 0.66 | ||||
Ultimate Elongation at Break | % | 375 |