High quality fireproof refractory cement per ton price supplier
Features:
1. Quick hardening and early strengthening
2. Used for urgent repairing
3. Used for project done in winter
4. Stable corrosion resistance from surface effect
5. Anti-freezing
6. High purity
Notes: refractory cement = high alumina cement = aluminate cement
There are many kinds of refractory cement, please consult us online or by email with its using environment condition, we will recommend you the most suitable one according to your request.
Physical & Chemical Indexes:
CA-50 |
Physical Property |
Chemical Composition |
||||||||||
Rupture Strength MPa |
Compressive Strength MPa |
Setting Time Min. |
Al2O3 |
SiO2 |
Fe2O3 |
R2O (Na2O+0.658K2O) |
||||||
1day |
3days |
28days |
1day |
3days |
28days |
Initial time |
Final time |
|||||
5.5 |
6.5 |
/ |
40 |
50 |
/ |
≥30 |
≤360 |
50-60 |
≤8.0 |
≤2.5 |
≤0.4 |
CA-60 |
Physical Property |
Chemical Composition |
||||||||||
Rupture Strength MPa |
Compressive Strength MPa |
Setting time Min. |
Al2O3 |
SiO2 |
Fe2O3 |
R2O (Na2O+0.658K2O) |
||||||
1day |
3days |
28days |
1day |
3days |
28days |
Initial time |
Final time |
|||||
2.5 |
5.0 |
10.0 |
20 |
45 |
80 |
≥60 |
≤1080 |
60-68 |
≤5.0 |
≤2.0 |
≤0.4 |
CA-70 |
Physical Property |
Chemical Composition |
||||||||||
Rupture strength MPa |
Compressive strength MPa |
Setting time Min. |
Al2O3 |
SiO2 |
Fe2O3 |
R2O (Na2O+0.658K2O) |
||||||
1day |
3days |
28days |
1day |
3days |
28days |
Initial time |
Final time |
|||||
5.0 |
6.0 |
/ |
30 |
40 |
/ |
≥30 |
≤360 |
68-77 |
≤1.0 |
≤0.7 |
≤0.4 |
|
Specific area cm2/kg |
≥4000 |
CA-80 |
Physical Property |
Chemical Composition |
||||||||||
Rupture strength MPa |
Compressive strength MPa |
Setting time Min. |
Al2O3 |
SiO2 |
Fe2O3 |
R2O (Na2O+0.658K2O) |
||||||
1day |
3days |
28days |
1day |
3days |
28days |
Initial time |
Final time |
|||||
4.0 |
5.0 |
/ |
25 |
30 |
/ |
≥30 |
≤360 |
≥77 |
≤0.5 |
≤0.5 |
≤0.4 |
Application:
High alumina refractory cement CA-50 has ISO international quality certificate. According to different content of Al2O3, it can be divided into four types: CA-50, CA-60, CA-70 and CA-80. They are of advantages of longer setting time, high temperature resistance, better stability in air, rapid strengthening and they’re addictive-free and suitable for contacting all kinds of castable, like low cement refractory castable, refractory concrete, ramming mixes, gunning mixes, man-made marble bricks, etc.
Using Method:
It’s easy to use refractory cement. It can strengthen after blending with water without need to add other bond. Besides, we will offer you a detailed product construction manual according to specific product and its using environment.
Currently, our products have been used in many carbon burning furnaces, CFB boilers in power plant, cement rotary kilns, non-ferrous metal melting furnaces, blast furnaces, hot-blast furnaces, coking furnaces, steel ladles, glass melting kilns and other high temperature industries all over the world.
For more real case, please click | All Case > |
For more company information, please click | Contact Us > |
FAQ & Our Service
1.Are you a trader or manufacturer?
We are manufacturer, we have own factory.
2.Can you accept OEM or ODM?
Of course, Logo is also acceptable.
3.What is the delivery time?
About 10-20 days after the contract signing.
4.What is your payment methods?
T/T L/C D/P Paypal West Union and others.
SERVICE
1. Timely response : To your inquiry in 24 hours, quickly respond mails and provide solutions.
2. Free sample : Sample and trial order are accepted for the quality evaluation.
3. Shorter delivery time : Book the earliest vessel or plane to guarantee the delivery time.
4. Professional Services : Provide high temperature solutions and professionals installation and technology services for you.
Request for Quotation >> |