Product Introduction:
99% pure alumina Ceramic Ball, is equal Denstone®99 Support Media. It is in chemical composition99+% alpha alumina and a maximum 0.2wt% SiO2. Because of its high alumina content and low silica(SiO2), it's a very excellent and ideal product for high temperature and steam applications.
Xintao 99% pure alumina Ceramic Ball, has very excellent thermal properties, with its high density high-temperature resistance 1550℃, also it's a good choice for heat retention or equilibration media.
Typical Application: a) It's a very excellent and ideal product for high temperature and steam applications, such as secondary reformers in ammonia processing, where leached silica will coat downstream equipment or foul the catalyst bed.
b) It's suitable for applications in olefin processes, such as ethylene dryers, where there's the polymerization problem.
Warranty: By National Standard HG/T 3683.1-2014 .
Free consultation during the warranty period.
Model | 99% Pure alumina Ceramic Ball |
Color | White |
Shape | Ball |
Chemical composition | | Min. % | Max. % | Usual % |
Al2O3 | 99 | 99.6 | 99.3 |
SiO2 | / | 0.2 | 0.18 |
Fe2O3 | / | 0.2 | 0.02 |
TiO2 | / | 0.55 | 0.02 |
CaO | / | 0.1 | 0.2 |
MgO | / | 0.1 | 0.05 |
Na2O | / | 0.25 | 0.1 |
K2O | / | 0.2 | 0.13 |
Physical properties | Leachable Iron (%) | ≤0.01 |
Apparent Porosity by Weight (%) | ≤7.0 |
H2O absorption (wt.%) | <4.0 |
Acid resistance (%) | >99.8 |
Alkaline resistance (%) | ≥90 |
Bulk Density | (g/cm3) | 2.1 |
(lb/ft3) | 131 |
Specific density | (kg/m3) | 3400 |
(lb/ft3) | 212 |
Moh’s hardness (scale) | >8.0 |
Thermal conductivity (w/m2.k) | 0.7-0.8 |
Max. Operating Temperature | (℃) | 1550 |
(℉) | 2822 |
Thermal expansion (%) (500℃) | 0.10 |
Thermal Shock Stability (times) (1000℃ then water cooling) | 10 |
Geometric properties | Nominal Size | (mm) | 3 | 6 | 10 | 13 | 16 | 19 | 25 | 38 | 50 |
(inch) | 1/8 | 1/4 | 3/8 | 1/2 | 5/8 | 3/4 | 1 | 1.5 | 2 |
Crush Strength Min. | (lbs) | 115 | 230 | 440 | 1355 | 1720 | 3344 | 3432 | 4034 | 4960 |
(kg) | 52 | 105 | 200 | 615 | 780 | 1520 | 1560 | 1830 | 2250 |
(N/PC) | 510 | 1030 | 1961 | 6031 | 7650 | 14896 | 15288 | 17946 | 22065 |