Test Item | Unit | Lc1001 |
Appearance | - | White, Semiliquid |
Density Relative | g/cm3 | 1.6~1.65 |
Adhesion | Cps | 80000~90000 |
Surface drying time | min℃ | ≤10 |
Full curing time | d | 3-7 |
Curing type | One component deethanol type | |
Tensile Strength | MPa | ≥1.5 |
Elongation | % | 200~400 |
Hardness | Shore A | 35~45 |
Shear Strength | MPa | ≥1.0 |
Peel Strength | N/mm | ≥5 |
Linear Shrinkage | % | ≤0.5 |
Thermal Conductivity | W/m·K | 1 |
Volume Resistivity | Ω·cm | 3×1015 |
Dielectric strength | kV/·mm | 20 |
Dielectric Constant | 1.2MHz | 2.8 |
The above performance data are measured after curing at 25 ℃ and 55% relative humidity for 7 days.
Package specification: 100ml / 100 pcs / box, 300ml / 25 PCS / box, 2.6l/4 PCS / box
Storage: 1. The product shall be stored in a cool and dry environment below 35 ℃, and the storage period below 25 ℃ is 1 year
LC1001 Thermal Conductive Silicone Glue
LC1001 is the semi-flowing heat-resistant silicone adhesive sealant which is made of special silicone rubber material the addition of thermal powders. With excellent conductivity,V0 flame retardant grade, excellent temperature resistance, can be in the range of 60 ~ 280 ℃ Long-term use. As well as good adhesion, long term use will not fall off, will not produce Contact gap to reduce thermal conductivity, moisture-proof, anti-seismic, anti-leakage and aging .The properties are widely used for the adhesion and sealing of the electronic components with high thermal conductivity, which is a single part of the acetone oxime type, It can be cured silicone rubber and conforms to the requirements of ROHS REACH UL.
Typical Applications
High power LED lamps and lanterns, electrical power, microwave oven, electronic components and other industrial products of thermal conductive adhesive sealing, alternative thermal conductive silicone used in high-power electric module and radiator thermal conductivity between fixed filling adhesive, no card buckle screw, more reliable filling heat, simple process and lower cost.
Applying Process
1. Surface clean : Clean the surface of the adhesive object and remove the rust, dust and oil.
2. Sizing: Twist the cap of the hose, squeeze the gel into the clean surface, and make it natural.
3. Curing: Place the bonded or sealed parts in the air while them to solidify naturally. Curing is a process from surface to the internal, within 24 hours (at room temperature and 55% relative humidity) will cure the depth of the 2 ~ 4 mm, if the site location is deeper that completely curing time will be postpone, especially it is not easy to come into contact with air. if the temperature is low, cure time also will be postpone .Prior to further processing or wrapping the bonded parts, it is recommended that the user wait long enough to ensure that the adhesion and integrity of the adhesion are not affected.
Note: After the operation is completed, the unused glue should be tightened immediately and sealed. When used again, if the seal has a little bit of skin, remove it. In the process of storage, a small amount of curing phenomenon may occur in the pipe mouth, which can be used normally unaffected the product performance.
Why choose us?
1.10 years TIMs experiences.
2.Professional R&D team.
3.One-stop service for thermal conductive materials.
4.Better quality and better price.
5.We cooperate with PHILIPS,SKYWORTH,HUAWEI, TCL etc.
6.Our products meet ROHS,REACH and safety standards certification standards.
7.All of our products thermal conductivity under reality test.
Q1:Can I get free samples?
A1:Yes,we are so glad to provide you with free samples.
Q2: Is there any discount?
A2:Yes,for larger quantity,we always offer better price.