HSS H7 Morse Taper Shank Machine Reamer with TIN coating
Type of front end with edge angle of in clination are ordered according to non-standard .
Outside Dia. | Overall Length | Flute Length | No. |
10 | 140 | 22 | 1 |
11 | 140 | 22 | 1 |
12 | 105 | 25 | 1 |
13 | 105 | 25 | 1 |
14 | 160 | 25 | 1 |
15 | 160 | 25 | 2 |
16 | 170 | 25 | 2 |
17 | 170 | 25 | 2 |
18 | 180 | 28 | 2 |
19 | 180 | 28 | 2 |
20 | 190 | 28 | 2 |
21 | 190 | 28 | 2 |
22 | 200 | 28 | 2 |
23 | 200 | 28 | 2 |
24 | 220 | 28 | 3 |
25 | 220 | 28 | 3 |
26 | 230 | 30 | 3 |
27 | 230 | 30 | 3 |
28 | 240 | 30 | 3 |
30 | 240 | 30 | 3 |
32 | 240 | 30 | 3 |
Reamer series : Taper shank , straight shank machine reamer , taper pin reamer , taper reamer, complex reamer.
Production process of HSS morse taper shank machine reamer :
Material Introduction:
A. W6Mo5Cr4V2 (GB) M2( ASTM), S6-5-2(DIN), SKH51(JIS)
chemical composition:C 0.85, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 6.00, Mo 4.80 V 1.85
main application:It is widely used for making all kinds of cutters and durability cold-work die
B. W6Mo5Cr4V2Co5 (GB), M35( ASTM), 1.3243(DIN), SKH55(JIS)
chemical composition: C 0.93, Si 0.38, Mn 0.35, P≤0.030, S≤0.030, Cr 4.10, W 6.30, Mo 4.80 V 1.85, Co 5.00
main application:It is often used for making blades with high-speed and great cutting difficulty as it’s good abrasive resistance
W6Mo5Cr4V2(M2),W9Mo3Cr4V(W9),W18Cr4V(W18),W6Mo5Cr4V2Al(M2Al),W6Mo5Cr4V2Co5(M35),W2Mo9Cr4VCo8(M42),W4Mo3Cr4VSi(4341),W4Mo2Cr4VSi(4241)