HS221 brass brazing rod 2.4mm 3.2mm best price
Product Name: HS221 Brazing TIG rod
Product specifications: 1.6MM, 2.0MM, 2.5MM, 3.0MM,3.2MM,4.0MM
Product application: Brazing wire refers to the application of copper and copper alloy welding materials, suitable
for oxygen-acetylene, TIG, MIG welding, widely used in automotive, shipbuilding, electrical and other manufacturing
industries.Product performance and advantages: It can effectively eliminate pores, low melting point, excellent
welding process performance, good weld formation, high mechanical properties and good crack resistance.
HS221 brass brazing rod 2.4mm 3.2mm best price
Packing:5kg/unit
Diameter: 1.6MM, 2.0MM, 2.5MM, 3.0MM,3.2MM,4.0MM
Length:1000mm
Composition: CU=59-61%; Sn=0.5-1.0%; Si=0.15-0.35%; Zn balance.
HS221 brass brazing rod 2.4mm 3.2mm best price
Description: S221 has a melting point of about 890-905 C, is a special brass wire containing a small amount of tin
and silicon. Tin can improve the fluidity of the wire, and silicon can effectively control the evaporation of zinc and
eliminate the pores, thus obtaining a good weld.Uses: It is suitable for filling materials in brass and copper gas
welding, and is also widely used in brazing steel and cast iron and inlaid carbide tools. It can also be used as
a surfacing material for low pressure valve sealing surfaces and light load wear surfaces.
Welding powder: CJ301, QJ302
Comply with: GB/T9460-2008 Model SCu6810A
HS221 brass brazing rod 2.4mm 3.2mm best price
Remarks:
1. The welded parts of the weldment and the surface of the welding wire must be carefully cleaned before welding;
2. before welding, generally preheating to 400~500 C after welding, oxygen-acetylene flame welding must be equipped
with copper gas welding flux;
3. The welding flame should adopt neutral flame or slight oxidation flame, appropriately reduce the temperature during
welding, increase the welding speed, minimize the residence time of the molten pool at high temperature, and reduce
the evaporation and oxidation of zinc.