HDPE blow molding RESIN VIRGIN
Specification: LLDPE Film Grade
|
Item |
Test condition |
Test Method |
Value |
Unit |
|
Density |
|
ISO 1183 |
0.944-0.955 |
g/cm3 |
|
MFR |
190°C/2.16kg |
ISO 1133 |
0.03-0.07 |
g/10min |
|
Tensile strength at yield |
|
ISO 527-2 |
22 |
MPa |
|
Elongation at break |
|
ISO 527-2 |
>350 |
% |
|
ESCR |
F50,50°C,100% |
ASTM D-1693A |
1000 |
h |
|
VICAT |
|
ASTM D-1525 |
126 |
°C |
Blow Molding Grade
|
Item |
Test Condition |
Test Method |
Value |
Unit |
|
Density |
|
ISO 1183 |
0.950~0.955 |
g/cm |
|
MFR |
190°C/2.16kg |
ISO 1133 |
1.7~2.5 |
g/10min |
|
Tensile strength at yield |
|
ISO 527-2 |
24 |
MPa |
|
Elongation at break |
|
ISO 527-2 |
>600 |
% |
Injection Grade
|
Item |
Test Condition |
Test Method |
Value |
Unit |
|
MFR |
190°C/2.16kg |
ASTM D-1238 |
20 |
g/10min |
|
Density |
--- |
ASTM D-792 |
0.954 |
g/cm3 |
|
Tensile strength at yiled |
--- |
ASTM D-638 |
28 |
MPa |
|
Elongation at break |
--- |
ASTM D-638 |
250 |
% |
|
Impact tensile strength |
--- |
ASTM D-1822 |
42 |
kJ/m2 |
|
ESCR |
|
ASTM D-1693 |
3 |
--- |
|
VACIT |
--- |
ASTM D-1525 |
127 |
°C |
Application:
LLDPE is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.
- Step 1Find your interested products by search keywords
- Step 2Contact the supplier by clicking ”Enquire” or “request meeting” button, otherwise, you also could consult our import consultant.
- Step 3After verifying your email, get response from suppliers or our trade manager will contact you as soon as possible
- Step 4Set up meeting with the Chinese supplier without language barrier