Product Name | MBA-S Bitumen-based UV-resistant Waterproofing Membrane |
Material | Bitumen |
Color | Black |
Composed of aluminum-plastic composite surface film(UV resistant), innovative special rubberized asphalt and backed release paper, MBA-S Post-applied Waterproofing Membrane is a superb membrane designed to deliver premium in-place performance for different application environment. To install the membrane by full adhering method, the composite film can reduce surface temperature to prevent membrane from shrink, wrinkle and bulge caused by UV exposure.
Total thickness (mm) |
Width (m) |
length (m) |
Remark |
1.5 |
1.0 |
20 |
Other specification can be offered upon requirements |
2.0 |
1.0 |
20 |
Superior physical properties: high tensile strength, flexible seal around nails and cracks, compatible with different substrates.
Cold-applied: no flame hazard, self-adhered asphalt result in firm bonding and continuous overlapping.
High performance aluminum-plastic composite surface film: this can reduce surface temperature to prevent membrane from shrink, wrinkle and bulge caused by UV exposure.
Flexible and ease of use in detailed areas, together with other waterproofing.
Convenience of repairing membranes: water will not migrate even any leakage occurs due to firm bonding to substrate, so fast detecting of damaged membrane and immediate repairing.
Applicable to waterproofing to the basements and concrete or wooden roof decks of industrial and residential buildings;
Also suited for waterproofing of municipal engineering, such as subways and utility tunnels.
Property |
Value |
|||
1 |
Thickness/ mm |
≥1.5 |
||
2 |
Tensile Properties |
Tensile force /(N/50mm) |
Longitudinal |
≥300 |
Transverse |
||||
Elongation at break/ % |
Longitudinal |
≥50 |
||
Transverse |
||||
3 |
Tear Force(N) |
Longitudinal |
≥20 |
|
Transverse |
≥20 |
|||
4 |
Peel Strength between Membranes(N/mm) |
No treatment |
≥1.0 |
|
Heat treatment |
≥0.8 |
|||
5 |
Dimensional Change Rate/ % |
Longitudinal |
≤±1.0 |
|
Transverse |
||||
6 |
Peel Strength (bond to cement mortar) /(N/mm) |
No treatment |
≥1.5 |
|
Heat treatment |
≥1.0 |
|||
7 |
Heat Aging (80°C,168h) |
Tensile retention/% |
≥90 |
|
Elongation retention/% |
≥80 |
|||
Low Temperature Flexibility |
No crack at -18°C |
|||
8 |
Bonding Retention /min |
≥30 |
||
9 |
Heat Resistance |
70°C, 2h, no blister or flow |
||
10 |
Low Temperature Flexibility |
No crack at -20°C (-4°F) |
||
11 |
Water Impermeability |
No water leakage in 2 hours(0.3Mpa, 120min) |
||
REMARK:All the test items according to China Standard GB/T 35467-2017. |
Q: Is sample free?
A: Yes , sample of less than 1M2 or 1KG will be free of charge subject to buyer paying for freight cost, which can be returned when there is an firm order.
Q: Could I use my own shipping agent ?
A: Yes , your agent will be welcomed.
Q:Is the price negotiable?
A: A favourable discount will be given if the order in large quantity.