size: 20mm*20mm
glass thickness: 2.2mm/3mm
sheet resistance: 12~14ohm/sq
6ohm/sq
transmittance: >84%
package: 200piece/box
Welcome to TradeChina
FTO / ITO kaplamalı condudtive slaytlar cam dayanıklı güçlü asit elektrik iletken düşük direnç laboratuvar için
FOB Reference Price
Purchase quantity ()
Minimum order quantity
Payment
Meo Food Co., Ltd.
China - Hangzhou
Trading Company
Trade Capacity
Export Percentage
0-30%
Nearest Port
Penang, Valparaiso,Jetta
Accepted Delivery Terms
Employees
501-1000 people
Accepted Payment Currency
USD,EUR
Average Lead Time
5 Day(s)
Certifications
Product Specifications
--Product Description
Production Capacity :ITO/FTO laser etching & cutting
Etching minimum line width: 10μm~20μm / Etching minimum pitch:25μm~30μm
ITO glass processing hole diameter: 0.08mm-90mm / Cutting accuracy:20μm
We can provide you with customized services at any time,
Processing specifications:
1. Thickness range: 0.5MM-4.0MM; (Special thickness: 0.33-0.4MM, can be negotiated with the shopkeeper);
2. Specification range: 2MM-1200MM (tolerance: +-0.1MM);
3. Processing technology: cutting, etching, polishing, drilling, steel, grinding;
4. Processing shape: round, square and special-shaped;
5. Processing types: ITO conductive glass, AZO conductive glass, FTO conductive glass, electronic grade glass, automobile grade glass, Glass-Aluminium lens, coated glass.
Conductive Glass Sheet for Lab.
Our ITO conductive glass has been widely used in new technology fields such as mobile phone screens, PDAs, calculators, electronic watches, electromagnetic shielding, photocatalysis, solar cells, biological experiments, domestic / Singapore / Hong Kong and other major university laboratories ；
We can provide customized services for ITO/FT0 glass, such as precision etching, cutting, drilling and other processing.
If you are looking for a strong supplier Please contact us
Skype : touchglass@aliyun.com
Phone/WhatsApp: 86 18925789558
e-mail: 591104604@qq.com / wangdaohua888@gamil.com
WeChat: wangaihuax2017
Skype : touchglass@aliyun.com
Phone/WhatsApp: 86 18925789558
e-mail: 591104604@qq.com / wangdaohua888@gamil.com
WeChat: wangaihuax2017
Precision etching
Shaped cutting
Laser precision drilling
Specifications & packaging
Parameter Information
Product Name | ITO/FTO/AZO Conductive Glass | ||||||||
Size | Customzied as request | ||||||||
Thickness | 0.2-3mm | ||||||||
Conductive Value | 3ohm, 5ohm, 7ohm, 8ohm, 10ohm, 15ohm, 20ohm, 30ohm, 50ohm, 70ohm, 100ohm, 150ohm, 300ohm and etc. | ||||||||
Thickness Tolerance | +/-0.05mm | ||||||||
Flatness | ≦0.10% | ||||||||
Product Introduction
ITO Conductive Glass
1. ITO conductive glass is manufactured by depositing silicon dioxide (SiO2) and indium tin oxide (commonly referred to as ITO)
thin films on the basis of soda-lime or borosilicate glass by using a magnetron measurement method.
thin films on the basis of soda-lime or borosilicate glass by using a magnetron measurement method.
2. ITO is a metal compound
with good transparent and conductive properties. It has the characteristics of forbidden bandwidth, high light transmittance and
low resistivity in the visible spectrum region. It is widely used in affirmative display devices, solar cells, and special
functional window coatings. Laboratory equipment and other optoelectronic devices.
with good transparent and conductive properties. It has the characteristics of forbidden bandwidth, high light transmittance and
low resistivity in the visible spectrum region. It is widely used in affirmative display devices, solar cells, and special
functional window coatings. Laboratory equipment and other optoelectronic devices.
FTO Conductive Glass
1. FTO conductive glass is fluorine-doped SnO2 transparent conductive glass (SnO2: F), referred to as FTO.
2. SnO2 is a wide
band-gap oxide semiconductor that is transparent to visible light, with a band gap of 3.7-4.0eV, and has a regular tetrahedral
gold red structure. After being doped with fluorine, the SnO2 film has the advantages of good light transmittance to visible
light, large ultraviolet absorption coefficient, low resistivity, stable chemical properties, and strong resistance to acid and
alkali at room temperature.
band-gap oxide semiconductor that is transparent to visible light, with a band gap of 3.7-4.0eV, and has a regular tetrahedral
gold red structure. After being doped with fluorine, the SnO2 film has the advantages of good light transmittance to visible
light, large ultraviolet absorption coefficient, low resistivity, stable chemical properties, and strong resistance to acid and
alkali at room temperature.
ITO GLASS LIST | ||
thickness | Sheet resistance | |
1.1mm | 3ohm/sq~100ohm/sq | |
3mm | 4~6ohm/sq and 3~5ohm/sq | |
4mm | 25ohm/sq | |
0.4/0.5/0.7/0.8/1.0/1.5/1.8/2mm | 7~10ohm/sq | |
FTO GLASS LIST | ||
1.1mm | 15~20ohm/sq | |
1.6mm | 14~15ohm/sq | |
2.2mm | 7~8ohm/sq; 6~10ohm/sq; 14~15ohm/sq | |
3.0mm | 12~14ohm/sq | |
4.0mm | 12~14ohm/sq | |
Equipment Resources
We now have two companies in the conductive materials and glass industries, namely Dongguan Qunguan Electronic Technology Co., Ltd. and Huasheng Glass Co., Ltd. We have advanced equipment and skilled workers, and the first picosecond laser machine in the industry Cutting and etching the glass, the processing accuracy can reach 0.02mm, which can meet the needs of various scientific research institutions for top products. We can provide customized services for various scientific research institutions, such as drilling and etching of conductive glass and conductive film .
ITO glass parameters
Product Name: | ITO coated glass substrate, ITO conductive glass slide | ||||||
Other Names: | Indium Tin Oxide glass, Indium Tin Oxide thin film glass, Indium Tin Oxide conductive glass, ITO thin film coated glass | ||||||
Standard Size (Length × width): | 1" x 3" (25.4x76.2 mm), 1" x 1" (25.4x25.4 mm), 10 x 10 mm, 50 x 50 mm, 100 x 100 mm, 300 x 300 mm (Or specific size, according to customer's requirements) | ||||||
Standard Thickness: | 0.7mm or 1.1mm or 0.55mm or 2.0mm or 3.0mm | ||||||
Resistance : | 4~5 ohm/sq, 6~8 ohm/sq,10~15 ohm/sq,20~30 ohm/sq, 30~40 ohm/sq, 60~80 ohm/sq, 80~100 ohm/sq, 300~500 ohm/sq, or others | ||||||
Transmittance: | >83%, >84%, >85%, >86% | ||||||
ITO thin Film thickness: | 185nm ( 6~8 ohm/sq); 135nm ( 10~15 ohm/sq) | ||||||
Glass substrate | Soda-lime glass | ||||||
Application: | Mobile phone screens, PDAs, calculators, electronic watches, electromagnetic shielding, photocatalysis, solar cells, biological experiments, major university laboratories and other new scientific and technological fields; | ||||||
Product Name | Thickness | Resistance | ITO thin film | Transmittance | Standard Size |
ITO glass | 1.1mm, 0.7mm, 0.55mm | 4~5 ohm/sq | 260nm | >83% | 10 x10mm 20 x20mm 25 x25mm 1” x1”inch 50 x50mm 25 x75mm 1” x3”inch 100x100mm 300x300mm |
1.1mm, 0.7mm, 0.55mm | 6~8 ohm/sq | 185nm | >84% | ||
1.1mm, 0.7mm, 0.55mm | 10~15 ohm/sq | 135nm | >86% | ||
1.1mm, 0.7mm, 0.55mm | 15~20 ohm/sq | 95nm | >85% | ||
1.1mm, 0.7mm, 0.55mm | 20~30 ohm/sq | 65nm | >80% | ||
1.1mm, 0.7mm, 0.55mm | 30~40 ohm/sq | 50nm | >82% | ||
1.1mm, 0.7mm, 0.55mm | 40~60 ohm/sq | 35nm | >85% | ||
1.1mm, 0.7mm, 0.55mm | 60~80 ohm/sq | 30nm | >86% | ||
1.1mm, 0.7mm, 0.55mm | 80~100 ohm/sq | 23nm | >87% | ||
1.1mm, 0.7mm, 0.55mm | 300~500 ohm/sq | 13nm | >88% |
ITO glass spot trading Orders can be placed quickly and shipped quickly，The following table is the spot parameters (Other specifications products are produced according to customer requirements, within 2000 pieces, and the delivery time does not exceed one week)
Product Code | Description | L x W x Thickness | Surface Resistivity | ||
ITO 5001 | Indium Tin Oxide coated Glass | 25mm × 25mm × 1.1mm | ~10 ohms/sq | ||
ITO 5002 | Indium Tin Oxide coated Glass | 50mm × 25mm × 1.1mm | ~10 ohms/sq | ||
ITO 5003 | Indium Tin Oxide coated Glass | 75mm × 25mm × 1.1mm | ~10 ohms/sq | ||
ITO 5004 | Indium Tin Oxide coated Glass | 50mm × 50mm × 1.1mm | ~10 ohms/sq | ||
ITO 5005 | Indium Tin Oxide coated Glass | 100mm × 100mm × 1.1mm | ~10 ohms/sq | ||
ITO 5006 | Indium Tin Oxide coated Glass | 25mm × 25mm × 1.1mm | ~10 ohms/sq | ||
ITO 5007 | Indium Tin Oxide coated Glass | 25mm × 25mm × 1.1mm | ~25 ohms/sq | ||
ITO 5008 | Indium Tin Oxide coated Glass | 50mm × 25mm × 1.1mm | ~25 ohms/sq | ||
How to use and store conductive glass
1. When taking and putting it down, it can only touch the four sides, not the conductive glass ITO surface;
2. Handle with care, not collide with other fixtures and machines;
3. If you store for a long time, you must pay attention to moisture, so as not to affect the resistance and transmittance of the glass; ITO conductive glass
2. Handle with care, not collide with other fixtures and machines;
3. If you store for a long time, you must pay attention to moisture, so as not to affect the resistance and transmittance of the glass; ITO conductive glass
Conductive glass cleaning
During the production, packaging, and transportation of ITO/FTO conductive glass, the surface of the glass may be contaminated by impurities such as dust or grease. Before using ITO/FTO conductive glass, it is necessary to clean it. There are many cleaning methods, the most commonly used is ultrasonic cleaning with organic solvents. Grease stained on the glass surface is insoluble in water, but it is soluble in organic solvents such as toluene, acetone, and ethanol.
Among them, toluene has the strongest degreasing ability, so first clean with toluene, but toluene will remain on the glass surface. Since toluene is soluble in acetone, it can be cleaned with acetone, which not only cleans out the residual grease, but also dissolves toluene. Similarly, acetone will remain on the glass surface. Since acetone is soluble in ethanol, continue to clean with ethanol. Ethanol and water dissolve each other in any ratio, and then use a large amount of deionized water to dissolve the ethanol, and finally put it in anhydrous alcohol for storage, and then take it out for use when it is used, so that many tablets can be washed at one time.
order：
Toluene（10--20min）→ acetone（10—20min）→ Ethanol（10—20min）→ Deionized water（20—30min） Perform ultrasonic cleaning in the above
order,
Finally, preserved in anhydrous alcohol, can be stored for a long time
Among them, toluene has the strongest degreasing ability, so first clean with toluene, but toluene will remain on the glass surface. Since toluene is soluble in acetone, it can be cleaned with acetone, which not only cleans out the residual grease, but also dissolves toluene. Similarly, acetone will remain on the glass surface. Since acetone is soluble in ethanol, continue to clean with ethanol. Ethanol and water dissolve each other in any ratio, and then use a large amount of deionized water to dissolve the ethanol, and finally put it in anhydrous alcohol for storage, and then take it out for use when it is used, so that many tablets can be washed at one time.
order：
Toluene（10--20min）→ acetone（10—20min）→ Ethanol（10—20min）→ Deionized water（20—30min） Perform ultrasonic cleaning in the above
order,
Finally, preserved in anhydrous alcohol, can be stored for a long time
Packaging & Delivery
Packaging Details: double side protective film, wraped by kraft paper,
then in Polywood case.
Port: Shenzhen
Inner packaging.
Vacuum packaging is more convenient for transportation and storage. If the vacuum disappears, it will not affect storage. There is moisture-proof tissue inside..
If you still need ITO conductive film, please click this picture.
If you need to etch conductive glass, please click this picture.
Click on the picture
Conductive glass cleaning rack
Click on the picture
Flexible interdigital electrode
No desirable products?
Sourcing assistant>
How to start your business
- Step 1Find your interested products by search keywords
- Step 2Contact the supplier by clicking ”Enquire” or “request meeting” button, otherwise, you also could consult our import consultant.
- Step 3After verifying your email, get response from suppliers or our trade manager will contact you as soon as possible
- Step 4Set up meeting with the Chinese supplier without language barrier
Related Categories
EarthworkProductsFireplaces,StovesFlooring&AccessoriesMouldingsMultifunctionalMaterialsPlasticBuildingMaterialsPopular Searches
wiping ragswindow glassfolding legdrilling foamwelding platenfolding slidekindling bagsq railing glassfolding rodswelding glovesdecal pint glasshigh rise building glassslimming plastercogo building blocksmixing vatsbuilding materialsaqua drinking glassgrinding meshplan glassceiling osbfolding penswelding chapsrailing gateteflon glassfolding gatebuilding hoardingsundae glasshurling gamelion glassspalding ballcity building blocksfishing hatsfolding sunglassesbuilding cornicesloz building blocksceiling flagsspinning lampsgatling laserbuilding paperbirds glass