Test item | Index |
Surface drying | ≤6 |
Full drying | ≤24 |
Tensile strength(Mpa) | ≥9 |
Bending strength | ≥7 |
Compressive strength | ≥85 |
Shore hardness | ≥70 |
Flow Fairness, cm | ≥5min |
Abrasive resistance (750g/500r) | ≤0.02 |
60% H₂SO₄ resistant | No effervescent, break off, or slight discoloration |
25% NaOH resistant | No effervescent, break off, or slight discoloration |
3% NaCl-moist resistant | No effervescent, break off, or slight discoloration |
Gasline of 120# resistan | No effervescent, break off, or slight discoloration |
Adhesion strength (Mpa) | No effervescent, break off, or slight discoloration |
Test item | Method & Requirement | Reference dosage |
Base Treatment | 1. To clean the base surface, and polish with a professional grinder; | |
2. To deal with the shell, crack, hemp, loose, empty drum phenomena | ||
Bottom coating | 1.Apply professional rollers for epoxy self-flow flat primer evenly on the floor surface. | 0.15kg/m2 |
2.Requires vertical construction, without missing parts | 0.15kg/m2 | |
Middle Mortar coating | 1. To stir the epoxy self-leveling (Color paint-yellow bucket )well. | 0.9kg/m2 |
2.Add the curing agent (curing agent-blue bucket) to the color paint bucket (in 5: 1 ratio), and add the appropriate amount of quartz sand to stir fully into a paste; | ||
3.Use a professional blade to scrape 2 times (approximately 8-hour interval ). | ||
Sealing coating | 1. To stir the epoxy surface paint (Color paint-yellow bucket )well. | 0.1kg/m2 |
2.Add the curing agent (curing agent-blue bucket) to the color paint bucket (in 5: 1 ratio), and add the appropriate amount of quartz sand to stir fully into a paste; | ||
3.Use a professional blade to scrape 2 times (approximately 8-hour interval ). | ||
Surface coating | 1. To stir the epoxy surface paint (Color paint-yellow bucket )well. | 2kg/m2 |
2.Add the curing agent (curing agent-blue bucket) to the color paint bucket (in 6.5: 1 ratio), and stir fully ; | ||
Surface coating | 3.Use a professional blade to scrape 1 times(approximately 8-hour interval ). |