Welding of 0Cr13 stainless steels and similar steels, also surfacing for resistance to corrosion and abrasion
Features:
1) Welding temperature is lower than 300 degrees
2)Chemical composition of deposited metal:
C<=0.12 Mn<=1.0 Si<=0.9 S<=0.03 P<=0.04 Cr=11-13.5 Ni<=0.7 Mo<=0.75 Cu<=0.75Stainless steel structure
Inner packing:
1) 2.5mm x 300mm, 1-5kg/inner box + plastic bag
2) 3.2mm x 350mm, 1-5kg/inner box + plastic bag
3) 4.0mm x 350mm, 1-5kg/inner box + plastic bag
E410-16 is coating calcium titanate tape of stainless steel rod,the deposited metal of 13Cr steel. Has excellent oxidation resistance and corrosion resistance characteristics at high temperature,apply to Petroleum refining and chemical industry.
2.Applt to welding of the series of 410 or 420,high hardenability,the weld or heat - affected zone easy to crack.
Model Number | AWS E410-16 | |||||||
Brand Name | Ocean Welding | |||||||
Size | 2.0mm 2.5mm 3.2mm 4.0mm 5mm | |||||||
Applications | Welding of 0Cr13 stainless steels and similar steela,also surfacing for resistance to corrosion and abraion. | |||||||
Chemical composition of deposited metal(%) | ||||||||
C≤0.12 | Mn≤1.0 | Si≤0.9 | S≤0.03 | P≤0.04 | Cr11-13.5 | Ni0.07 | Mo≤0.75 | Cu≤0.75 |
Mechanical Properties
|
Tensile Strength(MPa) |
Elongation (%) |
standard value |
≥450 |
≥20 |
Example value |
495 |
44 |
Range of current: (AC or DC+)
Diameter & Length(mm) |
2.5*300 |
3.2*350 |
4.0*350 |
5.0*350 |
|
Range of current |
Downward welding |
50-85 |
80-120 |
100-160 |
150-200 |
(Amp) |
Overhead welding |
45-80 |
70-110 |
90-135 |
----- |