GENERAL INFORMATION | ||||||||
BRAND:LG CHEM | GRADE:PA66+GF30% LUMID GP2300B(W) | |||||||
FEATURES: | 1.GENERAL PURPOSE | |||||||
FORM: | PELLETS | |||||||
PROCESSING METHOD: | INJECTION MOLDING | |||||||
COLOR: | CUSTOMIZED COLOR |
Properties | Test Condition | Test Method | Unit | Typical Value | |
Physical | |||||
Specific Gravity | ASTM D792 | - | 1.37 | ||
Molding Shrinkage, 3.2mm | ASTM D955 | % | 0.4~0.9 | ||
Melt Flow Rate | ASTM D1238 | g/10min | |||
Water Absorption | 23℃, 24hrs | ASTM D570 | % | 1.1 | |
Mechanical | |||||
Tensile Strength, 3.2mm | ASTM D638 | ||||
@ Break | 5mm/min | kg/cm2 | 1,800 | ||
Tensile Elongation, 3.2mm | ASTM D638 | ||||
@ Break | 5mm/min | % | 2.9 | ||
Flexural Strength, 6.4mm | 3mm/min | ASTM D790 | kg/cm2 | 2,500 | |
Flexural Modulus, 6.4mm | 3mm/min | ASTM D790 | kg/cm2 | 87,500 | |
IZOD Impact Strength, 6.4mm | ASTM D256 | ||||
(Notched) | 23℃ | kg·cm/cm | 10 | ||
-30℃ | kg·cm/cm | ||||
Thermal | |||||
Melting Temperature | ASTM D3418 | ℃ | 260 | ||
Heat Deflection Temperature, 6.4mm | ASTM D648 | ||||
(Unannealed) | 18.6kg | ℃ | 255 | ||
4.6kg | ℃ | ||||
Coefficient of Linear Thermal Expansion | ASTM D696 | ||||
Flow | 10-5 m/m℃ | 3 | |||
Cross-flow | 10-5 m/m℃ | ||||
Ball Pressure Temperature | IEC 60695-10-2 | ℃ | |||
Burning Rate, 3.2mm | FMVSS 302 | mm | |||
Flammability | UL94 | ||||
0.75mm | class | HB | |||
1.5mm | class | HB | |||
3.0mm | class | HB | |||
Relative Temperature Index | UL 746B | ||||
Electrical | 120 | ℃ | |||
Mechanical with Impact | 110 | ℃ | |||
Mechanical without Impact | 120 | ℃ |