Alloy | Chemical Composition | ||||
QB | JIS /ASTM | Cu | P | O | Other |
T2 | JIS C1100 | 99.9 | 0.015-0.040 | - | balance |
TU | ASTM C10300 | 99.95 | 0.001-0.005 | - | balance |
TP1 |
JIS C1220 ASTM C12200 |
99.9 | 0.004-0.012 | - | balance |
Grade(China) | Grade(Japan) | Temper | Vickers Hardness (HV) | Tensile strength(Mpa) | Elongation(%) |
T2/T3/TP1/TP2 |
C11000/C1201 C1220.etc. |
M | - | ≥290 | ≥40 |
Y4 | 75-125 | 325~410 | ≥35 | ||
Y2 | 85-145 | 340~460 | ≥25 | ||
Y | 105-175 | 390~530 | ≥13 | ||
T | - | ≥490 | - |
0.5mm | 0.6mm | 0.7mm | 0.8mm | 1.0mm | 1.2mm |
1.5mm | 2.0mm | 3.0mm | 4.0mm | 5.0mm | 6.0mm |
8.0mm | 12mm | 15mm | 20mm | 25mm | 30mm |
35mm | 40mm | 45mm | 50mm | 55mm | |
We Can Customize Other Thicknesses, Please Contact US. |