Characteristic | Test Value | ||
Stain>0.3mm | None/m² | ||
D=(L+W)/2 | D≤0.2mm | ignore | |
0.2mm<D≤0.5mm | ≤5 Defects per M² | ||
0.5mm<D≤0.6mm | ≤2 Defects per M² | ||
D>0.6mm | None per M² | ||
L≥10mm | None per M² | ||
W≥0.1mm & L≥1mm | None per M² | ||
0.05mm≤W<0.1mm & 5mm≤L<10mm | None per M² | ||
0.05mm≤W<0.1mm & 1mm≤L<5mm | ≤5 Defects per M² | ||
Curl | <0.3'' (10”*10") | ||
Wrinkles/Creases | None |
Characteristic | Unit | Specification | Test Value(AVG) |
Overall thickness | mil(um) | 10mil(250um+/-5%) | 10mil(250um) |
Basic film thickness | mil(um) | 4mil optional grade PET Film (100um+/-3%) | 4mil(100um) |
Functional film thickness | mil(um) | 6mil(150um+/-5%) | 6.0mil(150um) |
PE or PP mask film/PET liner thickness | mil(um) | 2mil(50um+/-10%)/2mil(50um+/-5%) | 2.2mil(55um)/2mil(50um) |
Light transmittance | % | ≥94,≤95.8 | 95.5% |
Haze | % | <0.7 | 0.6% |
Reflectance | % | ≤0.9% Avg.(5°,450nm~700nm) | 0.9%(lowest Reflectance ≤0.8%) |
Top hardness of surface | Pencil Method H | ASTM D3363 | 3H |
Steel wool resistance | steel wool-100 Cycles 200 gram weight | 0.1% delta haze | |
Degree | H2O , AEE Method | 104° | |
Degree | Hexadecane AEE Method | 65° | |
Removal fingerprint property | AEE Method | very good | |
adhesive layer adhesion value | gram/inch | 2~3(To glass,nominal),AEE Method | 3 gram/inch |
Temperature resistance | 1hour at 130℃ & 30hours at 90℃ RH90% | no creep , no residual | |
Usage temperature | ℃ | Continuous usage | -25~80 |