Name | Custom Production Stainless Steel Sheet No.1 2B 2D Hairline BA Mirror 8K Finish 304 304L 316 316L 347 410 Stainless Steel Sheets |
Materials | 200series, 300series, 400series, 500series, 600series |
Thickness | 0.2~4mm, 4~20mm, 20~60mm, 60~115mm, 115mm+ |
Width | 600~1250mm, 200~600mm, 20~200mm |
Surface Finish | No.1, 2D, 2B, No.4, HL, BA, 8K, or customized |
200 SERIES STAINLESS STEEL | ||
Low-cost alternative to 300 series, low nickel content, worse corrosion resistance than 300 series. | ||
201 | Chemical element content :C:≤0.15; Si:≤1.00; Mn:5.5~7.50; Cr :16.0~18.0; P:≤0.060; S:≤0.030; Ni: 3.5-5.5 | |
Yield strength ≥275 Mpa ; Tensile strength ≥520 Mpa. | ||
202 | Chemical element content :C:≤0.15; Si:≤1.00; Mn:7.5~10.0; Cr :17.0~19.0; P:≤0.060; S:≤0.030; Ni:4.0~6.0 | |
Yield strength ≥275 Mpa ; Tensile strength ≥520 Mpa. | ||
300 SERIES STAINLESS STEEL | ||
The 300 series are chromium-nickel stainless steels with high nickel content, good corrosion resistance, heat Resistance, and good processability and weldability. | ||
304 | Chemical element content :C:≤0.08; Si:≤1.00; Mn:≤2.00; Cr :18.0~20.0; P:≤0.045; S:≤0.030; Ni: 8.0~11.0 | |
Yield strength ≥205 Mpa ; Tensile strength 515~1035Mpa. | ||
304L | Chemical element content :C:≤0.03; Si:≤1.00; Mn:≤2.00; Cr :18.0~20.0; P:≤0.045; S:≤0.030; Ni: 8.0~11.0 | |
Yield strength ≥205 Mpa ; Tensile strength 520~1035Mpa. | ||
310 | Chemical element content :C:≤0.25; Si:≤1.50; Mn:≤2.00; Cr :24.0~26.0; P:≤0.045; S:≤0.030; Ni: 19.0~22.0 | |
Yield strength ≥205 Mpa ; Tensile strength 520Mpa. | ||
316 | Chemical element content :C:≤0.08; Si:≤1.00; Mn:≤2.00; Cr :16.0~18.5; P:≤0.035; S:≤0.030; Ni: 10.0~14.0; Mo:2.0~3.0 | |
Yield strength ≥310 Mpa ; Tensile strength 620Mpa. | ||
400 SERIES STAINLESS STEEL | ||
The nickel content of the 400 series is lower than that of the 300 series, the corrosion resistance is poor, and the price is relatively low. But it is widely used in places with low corrosion resistance and high hardness. | ||
410 | Chemical element content :C:≤0.15; Si:≤1.00; Mn:≤1.00; Cr :11.5~13.5; P:≤0.04; S:≤0.030; | |
Yield strength ≥205 Mpa ; Tensile strength ≥440Mpa. |