1:High purity alumina oxide 99%
2:Used for testing laboratory and a variety of industrial analysis
3:Max. working temperature 1800
4:High chemical etching resistance
Composition | AL97 | AL98 |
AL2O3 Content | 97% | 99.80% |
Color | White | Ivory |
Tensile | 30 Kpsi | 32 Kpsi |
Flexural | 55 Kpsi | 60 Kpsi |
Compressive | 300 Kpsi | 330 Kpsi |
Density | 3.7 g/cc | 3.92 g/cc |
Hardness | 13.8 HV, Gpa | 18 HV, Gpa |
Thermal Conductivity | 25 W/(m K) | 32 W/(m K) |
C.O.T.E. | 77 In / In°C (x10^7) | 78 In / In°C (x10^7) |
Working Temperature | 1500 °C | 1750 °C |
Dielectric Constant | 9.5 | 9.8 |
Volume Resistivity | >10^14 Ohm-cm | >10^15 Ohm-cm |
Dielectric Strength | 16 KV/mm | 20 KV/mm |
Processing Service | Moulding |
Shape | Arc,Conical,Cylinderical,Tubular,Tall form,Low form,Tall form |
Capacity | 10ml,20ml,30ml,50ml,100ml,150ml,200ml,300ml,350ml,500ml |
Advantage | high temperature and chemical corrosion |
Working temperature | 1600C,1700C,1800C |
Usage | Sintering and melting of glass, phosphors,ceramics or metals |
Density | 3.9g/cm3 |
Certificate | ISO |
Purity | 99% |
Size | Size Customized |
Package | Carton Box |