High Temperature Resistance, High Hardness, High Density, High Melting Point
Item Name | 7.0mm / 7.5mmx55mm 90%wnife Tungsten Rod Billet Bar For Making Darts |
Material | Tungsten nickel ferro alloy, tungsten nickel copper alloy, WniFe ,WNiCu |
Dimensions | as request, All parts will be machined as customer's drawing. |
Density | 16.85-18.85g/cm3 |
Grade | 90wnife(90wnicu), 93wnife(93wnicu), 95wnife(95wnicu), 97wnife(97wnicu) |
Standard | ASTM B777, AMST 21014 |
Application | CT machine parts, anti-radiation material |
AMST 21014 class 1 | AMST 21014 class 2 |
1. 90%WNiFe, 90%WNiCu 2. Density : 16.85-17.30 g/cm3 3. Hardness: 32HRC max 4. Elongation: 5 - 20% 5. Tensile Strength: 1470Mpa max 6. Impact Toughness:58J/cm2 max | 1. 92.5%WNiFe, 92.5%WNiCu 2. Density : 17.15-17.85 g/cm3 3. Hardness: 33HRC max 4. Elongation: 5 - 15% 5. Tensile Strength:1720Mpa max 6. Impact Toughness:54J/cm2 max |
AMST 21014 class 3 | AMST 21014 class 4 |
1. 95%WNiFe, 95%WNiCu 2. Density : 17.75-18.35 g/cm3 3. Hardness: 34HRC max 4. Elongation: 3 - 10% 5. Tensile Strength:971Mpa max 6. Impact Toughness:43J/cm2 max | 1. 97.5%WNiFe,97.5%WNiCu 2. Density : 18.25-18.85 g/cm3 3. Hardness: 35HRC max 4. Elongation: 1 - 8% 5. Tensile Strength:964Mpa max 6. Impact Toughness:22J/cm2 max |