CW102C free machining beryllium copper rod as per EN 12164 for relay parts

CW102C free machining beryllium copper rod as per EN 12164 for relay parts  

C17300 is a high performance copper alloy with free machining characteristics. It could minimize signal
distortion in coaxial RF connectors and reduce power loss in circular connectors and contact probes.

C17300 after machining and forming operations, could be easily heat treated and plated to obtain maximum mechanical and electrical performance.

APPLICATION:

In Electronic and Electrical Industry: probe cards, switch parts, relay parts, electrical connectors, fuse clips, contact bridges, electrical motor components, navigational instruments, electrical switch and relay blades.

FORM:

In straight rod or coiled wire. Length: up to 3m. Diameters range from 1.0 mm to 22.0 mm. Rod end
in pointed or(and) chamfered as required is made, depending on the diameter.

Surface condition: cold drawn and grinded surface free of any scratch, residues and cracks.

SPECIFICATION: ASTM B 196 EN 12164 

Chemical Composition:

Be: 1.8-2.0%
Co+Ni: 0.20% Min.
Co+Ni+Fe: 0.60% Max.
Lead: 0.20-0.60%
Cu: Balance
Note: Copper plus additions equal 99.5% minimum.

Related Standard :

Rods/Bars/Tubes: ASTM B196, QQ-C-530
Wires: ASTM B197, QQ-C-530,

Plates: ASTM B194

European Standards: DIN 2.1248, CW102C to EN 12164 

Other material are also available

C17200/CuBe2/CW101C/DIN 2.1247

C17500/CuCo2Be/CW104C/DIN 2.1285

C17510/CuNi2Be/CW110C/DIN 2.0850

CuCo1Ni1Be/CW103C