CAST STAINLESS STEEL SHOT

CAST STAINLESS STEEL SHOT

CAST STAINLESS STEEL SHOT

CAST STAINLESS STEEL SHOT is used in all applications where non-rusting materials such as aluminum, zinc, stainless steel, brass, bronze, etc. are blasted.

CAST STAINLESS STEEL SHOT’s large spectrum of grain sizes makes it perfect for cleaning, de-burring, hardening and surface finishing of all types of castings, forgings, profiles, wire and welded structural parts, without the possibility that rust could discolor the bright surface due to ferritic dust.

CAST STAINLESS STEEL SHOT distinguishes itself by having a high percentage of spherical grains and by its compactness. The end result is low consumption, high performance and low machine wear.

Chemical composition: C ~ 0,15%, Cr ~ 18%, Ni ~ 10%

Apparent density: ~ 4,7 g/cm³ (~ 293 lb/ft³)

Hardness: on delivery ~ 300 HV (~ 30 HRC), as operating mix ~ 475 HV (~ 47 HRC)

Microstructure: austenitic

Main fields of application:

Blast cleaning, deburring, surface finishing, surface-improvement

·       All types of aluminium castings and forgings

·       Zinc pressure die castings

·       Non-ferrous metals and special alloys

·       Stainless steel castings and forgings

·       Machinery and welded structures in stainless steel

Before cleaning with CAST STAINLESS STEEL SHOT

After cleaning with CAST STAINLESS STEEL SHOT

CAST STAINLESS STEEL SHOT offers the following advantages:

·       Great durability

·       Short blasting times

·       Bright appearance

·       Rust-free surfaces

·       Reduced wear of blast cleaning equipment

·       Low waste disposal costs

·       Dust-free blasting process

Blasting of metals...

·       For efficient deburring

·       For bright appearance

·       For surface preparation prior to coating

Executive standard for stainless steel shot production:

We produce stainless steel wire components in strict accordance with American SAE standards and Japanese JIS standards to produce stainless steel shot for sand blasting and shot blasting.

Main technical indexes of stainless steel shot:

(304 Austenite Type): (C)<0.15%, (Cr)=16~18%, (Ni)=6~10%, (Si)<1%, (Mn)<2%

(430 Ferrite Type): (C)<0.15%, (Cr)=16~18%, (Si)<1%, (Mn)<1%

(410 Martensite Type): (C)<0.15%, (Cr)=11~13%, (Si)<1%, (Mn)<1%