Melting Point (Liquidus) | 1980 °F | 1082 °C |
Melting Point (Solidus) | 1900 °F | 1038 °C |
Annealing Range (min - max), 1 hr | 1290 - 1380 °F | 700 - 750° C |
Density | 0.320 lb/in3 | 8.86 gm/cm3 |
Electrical Resistivity (Annealed) | 18.9 Ω·cir-mil/ft @ 68 °F | 3.13 µΩ·cm @ 20 °C |
Electrical Conductivity (Annealed) | 55% IACS @ 68 °F | 0.320 MS·cm @ 20 °C |
Thermal Conductivity | 146 Btu/ft2 /ft·hr/°F @ 68 °F | 253 W/m·K @ 20 °C |
Coefficient of Thermal Expansion | 9.8 x 10-6 per °F (68-572 °F) | 17.6 x 10-6 per °C (20-300 °C) |
Modulus of Elasticity (Tension) | 18,000 ksi | 124,000 MPa |
Modulus of Rigidity | 6,000 ksi | 41,000 MPa |