single venturi sand blast nozzles for sandblasting machine
Coarse thread long venturi boron carbide plastic jacket sand blast nozzles
1)bore diameter:6/8/10/12mm
2)length :130-230mm
Coarse thread long venturi boron carbide rubber jacket sand blast nozzles
Boron carbide nozzles offer the longest wear life of any standard nozzle material.
Peak nozzle production performance is maintained for longer periods with optimum consumption of air
and abrasive. Boron carbide nozzles typically outwear tungsten carbide nozzles by five to ten times
and silicon carbide by two to three times. Boron carbide nozzles are recommended for use with abrasives
such as aluminum oxide and aggressive mineral aggregates.
Our selection of nozzles is unmatched, anywhere
We have standard products that can replace the original nozzles installed on most equipment.
We also have higher performance upgrades for most OEM products to allow you to achieve optimum
blasting effectiveness, efficiency and reduce your total costs.
Approximate Nozzle Service Life in Hours *
Nozzle material Steel Shot and Grit Expendable Abrasives Alu-oxide Abrasives
Ceramic 20 - 40 10 - 30 1-4
Tungsten Carbide 500 - 800 300 - 400 20-40
Silicon Carbide / Nitride 600 - 1000 400 - 600 50-100
Boron Carbide 1500 - 2500 750 - 1500 200 – 1000
* Estimated values for comparison. Actual service life will vary depending upon
blast pressure, media size and particle shape.
different models as following :
Model |
Bore Dia |
Length |
Inlet |
HB-ABN-5 |
5mm(3/16) |
100mm(4) |
25mm(1) |
HB-ABN-6 |
6mm(15/64) |
125mm(4 7/8) |
25mm(1) |
HB-ABN-7 |
7mm(9/32) |
130mm(5 1/8) |
32mm(1 1/4) |
HB-ABN-8 |
8mm(5/16) |
145mm(5 1/16) |
32mm(1 1/4) |
HB-ABN9 |
9mm(23/64) |
175mm(6 7/8) |
32mm(1 1/4) |
HB-ABN-10 |
10mm(25/64) |
175mm(6 7/8) |
32mm(1 1/4) |
HB-ABN-11 |
11mm(7/16) |
180mm(7) |
32mm(1 1/4) |
HB-ABN-12 |
12mm(15/32) |
180mm(7) |
32mm(1 1/4) |
Main application:
widely used in Industrial production machines such as Sandblasting machines, hydraulic cutters, power plant boilers etc.
Advantage: High temperature resistance, Abrasion-resistance, light unit weight, working life much longer than tradition material.
B4C specifications:
Density: 2.40-2.65 g/cm3
Elastic modulus: 510 Gpa
Knoop Hardness: 3300
Flexural strength: 400-650 Mpa
Compressive strength: 4100 Mpa
Fracture toughness: 4.5-7.0 Mpa.m1/2
Coefficient of thermal expansion: 4.5x106
Thermal Conductivity: 29 m0k
Maximum permissible service temperature in air: 1500℃
Regular size list
Diameter(mm) |
Diameter (mm) |
Length(mm) |
20 |
4 |
35 |
20 |
6 |
35 |
20 |
8 |
35 |
20 |
10 |
35 |
Diameter(mm) |
Diameter (mm) |
Length(mm) |
20 |
4 |
45 |
20 |
6 |
45 |
20 |
8 |
45 |
20 |
10 |
45 |
Diameter(mm) |
Diameter (mm) |
Length(mm) |
20 |
6 |
60 |
20 |
8 |
60 |
20 |
10 |
60 |
Diameter(mm) |
Diameter (mm) |
Length(mm) |
20 |
6 |
80 |
20 |
8 |
80 |
20 |
10 |
80 |
Diameter(mm) |
Diameter (mm) |
Length(mm) |
21 |
8 |
82 |
21 |
10 |
82 |
21 |
12 |
82 |
Other sizes:
Diameter(mm) |
Diameter (mm) |
Length(mm) |
15 |
6 |
55 |
15 |
8 |
55 |
25 |
8 |
60 |
25 |
10 |
60 |
25 |
12 |
60 |
30 |
8 |
40 |
30 |
10 |
40 |
30 |
12 |
40 |
30 |
14 |
40 |
Material Comparation Chart:
Item |
Al2O3 |
SiC |
B4C |
Density |
3.5g/cm3 |
3.1g/cm3 |
2.4-2.65g/cm3 |
Hardness |
HV1650 |
HV2750 |
HV3300 |
Flexural strength |
290 Mpa |
380 Mpa |
400-650 Mpa |
Compressive strength |
850 Mpa |
3970 Mpa |
4100 Mpa |
Fracture toughness |
4.8 Mpa.m1/2 |
4.0 Mpa.m1/2 |
4.5-7.0 Mpa.m1/2 |
Thermal Conductivity |
20 m0k |
120m0k |
29 m0k |